PC LEXAN™ HFD4271 BK1G100L SABIC INNOVATIVE NANSHA
66
- Unit Price:
- $3731 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 42.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Hydrolysis resistance
- Application Areas:Electrical applications Mechanical accessories Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow : 3.20 mm | 内部方法 | 0.20 到 0.30 | % |
| Across Flow : 3.20 mm | 内部方法 | 0.40 到 0.50 | % | |
| Moisture Absorption | Saturation, 23°C | ISO 62 | 0.13 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.040 | % | |
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 15 | g/10 min |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 14.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | Yield 3 | ASTM D638 | 3.0 | % |
| Yield | ISO 527-2/5 | 3.0 | % | |
| Break | ISO 527-2/5 | 9.0 | % | |
| Flexural Modulus | 50.0 mm Span | ASTM D790 | 3300 | Mpa |
| Flexural Strength | Yield, 50.0 mm Span | ASTM D790 | 95.0 | Mpa |
| Tensile Strength | Yield 3 | ASTM D638 | 53.0 | Mpa |
| Yield | ISO 527-2/5 | 59.0 | Mpa | |
| Break 3 | ASTM D638 | 39.0 | Mpa | |
| Break | ISO 527-2/5 | 48.0 | Mpa | |
| Tensile Modulus | ASTM D638 | 3700 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ISO 306/B120 | 135 | °C | |
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 131 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 125 | °C | |
| Ball PressureTest | 123 to 127°C | IEC 60695-10-2 | 通过 | |
| Linear thermal expansion coefficient | Flow : -40 to 40°C | ASTM E831 | 4.0E-5 | cm/cm/°C |
| Flow : 23 to 80°C | ISO 11359-2 | 3.0E-5 | cm/cm/°C | |
| Across Flow : -40 to 40°C | ASTM E831 | 7.0E-5 | cm/cm/°C | |
| Across Flow : 23 to 80°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C | |
| RTI | UL 746 | 80.0 | °C | |
| RTI Imp | UL 746 | 80.0 | °C | |
| RTI Elec | UL 746 | 80.0 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 120 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 290 到 310 | °C | ||
| Mold Temperature | 70 到 95 | °C | ||
| Drying Time | 3.0 到 4.0 | hr | ||
| Suggested Shot Size | 40 到 60 | % | ||
| Rear Temperature | 265 到 290 | °C | ||
| Middle Temperature | 275 到 300 | °C | ||
| Front Temperature | 290 到 310 | °C | ||
| Nozzle Temperature | 280 到 305 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 40 到 70 | rpm | ||
| Vent Depth | 0.025 到 0.076 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 36.0 | J |
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 1700 | J/m |
| -30°C 6 | ISO 180/1U | 68 | kJ/m² | |
| 23°C 6 | ISO 180/1U | 93 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 100 | kJ/m² |
| 23°C | ISO 179/1eU | 110 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.0 | kJ/m² |
| 23°C | ISO 179/1eA | 18 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 0.40 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.