PC LEXAN™ SLX2271T NA9E166T SABIC INNOVATIVE SINGAPHORE
101
- Unit Price:
- $4918 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Aging resistance UV resistance Antistatic
- Application Areas:Lawn garden equipment Electronic and Electrical Electronic display Outdoor applications Lighting applications
- Color:--
- Grade:High liquidity level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.35 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 18 | g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 16.0 | cm3/10min |
| Outdoor Suitability | UL746C | f2 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Strength | ISO178 | 96.0 | Mpa | |
| Tensile Modulus | ISO527-2/1 | 2300 | Mpa | |
| Tensile Elongation | Break | ASTMD638 | >100 | % |
| Flexural Modulus | ISO178 | 2450 | Mpa | |
| Tensile Stress | Yield | ISO527-2/50 | 67.0 | Mpa |
| Break | ISO527-2/50 | 70.0 | Mpa | |
| Tensile Strain | Break | ISO527-2/50 | >100 | % |
| Yield | ISO527-2/50 | 6.0 | % | |
| Tensile Elongation | Yield | ASTMD638 | 6.0 | % |
| Tensile Modulus | ASTMD638 | 2400 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 67.0 | Mpa |
| Yield | ASTMD638 | 65.0 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 2450 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 96.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40to40°C | ISO11359-2 | 7E-05 | cm/cm/°C |
| MD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C | |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 124 | °C |
| Vicat Softening Temperature | ASTMD152510 | 139 | °C | |
| -- | ISO306/B50 | 139 | °C | |
| -- | ISO306/B120 | 140 | °C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 124 | °C |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 15 | kJ/m² |
| 23°C | ISO179/1eA | 65 | kJ/m² | |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 | kJ/m² |
| 23°C | ISO180/1A | 65 | kJ/m² | |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak | |
| UnnotchedIzodImpactStrength8 | 23°C | ISO180/1U | NoBreak | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 80.0 | J |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Transmittance | 2540µm | ASTMD1003 | 89.0 | % |
| Refractive index of light | ISO489 | 1.590 | ||
| Haze | 2540µm | ASTMD1003 | 0.60 | % |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 825 | °C |
| 2.0mm | IEC60695-2-13 | 825 | °C | |
| 2.5mm | IEC60695-2-13 | 825 | °C | |
| 3.0mm | IEC60695-2-13 | 825 | °C | |
| Flame Rating | 1.0mm | UL94 | V-2 | |
| Glow Wire Flammability Index | 1.6mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.