PC LEXAN™ 505RU WH8E261 SABIC INNOVATIVE NANSHA
77
- Unit Price:
- $3666 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Bromine free flame retard High transparency
- Application Areas:Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.40to0.60 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.30 | % |
Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 8.0 | g/10min |
Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 7.00 | cm3/10min |
Outdoor Suitability | UL746C | f1 |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Tensile Elongation | Break | ASTMD638 | 6.0 | % |
Flexural Modulus | ISO178 | 3500 | Mpa | |
Tensile Elongation | Yield | ASTMD638 | 4.0 | % |
Tensile Modulus | ASTMD638 | 3600 | Mpa | |
Tensile Strength | Break | ASTMD638 | 62.0 | Mpa |
Yield | ASTMD638 | 74.0 | Mpa | |
Flexural Modulus | 50.0mmSpan | ASTMD790 | 3200 | Mpa |
Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 114 | Mpa |
Tensile Modulus | ISO527-2/1 | 3500 | Mpa | |
Tensile Stress | Break | ISO527-2/5 | 60.0 | Mpa |
Yield | ISO527-2/5 | 72.0 | Mpa | |
Tensile Strain | Break | ISO527-2/5 | 6.0 | % |
Yield | ISO527-2/5 | 3.0 | % | |
Flexural Strength | ISO178 | 122 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Linear thermal expansion coefficient | MD:-40to40°C | ASTME831 | 5E-05 | cm/cm/°C |
MD:-40to40°C | ISO11359-2 | 5E-05 | cm/cm/°C | |
TD:-40to40°C | ASTME831 | 7.4E-05 | cm/cm/°C | |
TD:-40to40°C | ISO11359-2 | 8.5E-05 | cm/cm/°C | |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 137 | °C |
Vicat Softening Temperature | ASTMD152510 | 149 | °C | |
-- | ISO306/B50 | 147 | °C | |
-- | ISO306/B120 | 149 | °C | |
Ball PressureTest | 125°C | IEC60695-10-2 | Pass | |
Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 136 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Hot-wire Ignition | HWI | UL746 | PLC3 | |
High Amp Arc Ignition | HAI | UL746 | PLC0 | |
Comparative Tracking Index | CTI | UL746 | PLC3 | |
Comparative Tracking Index | IEC60112 | 175 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Unnotched Izod Impact Strength | -30°C | ISO180/1U | 73 | kJ/m² |
23°C | ISO180/1U | NoBreak | ||
Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 25.0 | J |
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7.0 | kJ/m² |
23°C | ISO179/1eA | 10 | kJ/m² | |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
23°C | ISO179/1eU | NoBreak | ||
Notched Izod Impact Strength | -30°C | ISO180/1A | 8.0 | kJ/m² |
23°C | ISO180/1A | 10 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 850 | °C |
3.0mm | IEC60695-2-13 | 875 | °C | |
UL flame retardant rating | 0.75mm,TestingbySABIC | UL94 | V-2 | |
1.5mm,TestingbySABIC | UL94 | V-0 | ||
3.0mm,TestingbySABIC | UL94 | 5VB5VA | ||
Glow Wire Flammability Index | 0.75mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.