PC LEXAN™ 4701R GN8B062TNS SABIC INNOVATIVE NANSHA

Unit Price:
$5057 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan transparent
Application Areas:Electronic and electrical
Color:--
Grade:High liquidity level

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24 hr	ASTM D570	0.19	%
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	2.0	g/10 min
Melt Mass-Flow Rate	Melt Mass-Flow Rate	300°C/6.1 kg	ASTM D1238	9.0	g/10 min
Specific Volume		ASTM D792	0.830	cm³/g
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.80 到 1.0	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	Break	ASTM D638	78	%
Flexural Modulus	50.0 mm Span	ASTM D790	2330	Mpa
Flexural Strength	Yield, 50.0 mm Span	ASTM D790	97.0	Mpa
Tensile Strength	Yield	ASTM D638	65.0	Mpa
Tensile Strength	Tensile Strength	Break	ASTM D638	77.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Specific Heat		ASTM C351	1260	J/kg/°C
Thermal Conductivity		ASTM C177	0.21	W/m/K
RTI		UL 746	130	°C
RTI Imp		UL 746	130	°C
RTI Elec		UL 746	130	°C
Coefficient of Linear Thermal Expansion (Flow)	-40 to 95°C	ASTM E831	8.1E-5	cm/cm/°C
Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	148	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		UL 746	PLC 3
Hot-wire Ignition		UL 746	PLC 2
High Amp Arc Ignition		UL 746	PLC 3
Dissipation Factor?	50 Hz	ASTM D150	1.6E-3
	Dissipation Factor?	60 Hz	ASTM D150	1.6E-3
	Dissipation Factor?	Dissipation Factor?	100 Hz	ASTM D150	0.026
Dielectric Strength	3.20 mm, in Air	ASTM D149	20	KV/mm
Dielectric Constant	60 Hz	ASTM D150	3.27
	Dielectric Constant	50 kHz	ASTM D150	3.27
	Dielectric Constant	Dielectric Constant	1 MHz	ASTM D150	3.10
Volume Resistivity		ASTM D257	> 2.5E+17	ohms·cm
High Voltage Arc Tracking Rate		UL 746	PLC 3
Arc Resistance		ASTM D495	PLC 6

Injection	Test Result	Unit
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	350 到 370	°C
Mold Temperature	80 到 115	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	325 到 350	°C
Middle Temperature	340 到 360	°C
Front Temperature	350 到 370	°C
Nozzle Temperature	345 到 365	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Tensile Impact Strength		ASTM D1822	577	kJ/m²
Gardner Impact	23°C	ASTM D3029	149	J
Unnotched Izod Impact Strength	23°C	ASTM D4812	3200	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTM D785	92
Rockwell Hardness	Rockwell Hardness	R-Scale	ASTM D785	127

optical performance	Test Condition	Test Method	Test Result	Unit
Transmittance	2540 µm	ASTM D1003	85.0	%
Refractive index of light		ASTM D542	1.600
Haze	2540 µm	ASTM D1003	1.0	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.