Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant Toughening UV resistance
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD:3.20mm	内部方法	0.40到0.80	%
Modeling Shrinkage	Modeling Shrinkage	TD:3.20mm	内部方法	0.40到0.80	%
Moisture Absorption	Saturation,23°C	ISO62	0.35	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.15	%
Melt Mass-Flow Rate	300°C/1.2kg	ASTMD1238	10	g/10min
Melt Volume flow Rate	300°C/1.2kg	ISO1133	9.00	cm3/10min
Outdoor Suitability		UL746C	f1

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	--6,7	ISO178	85.0	Mpa
Flexural Stress	Flexural Stress	Yield,50.0mmSpan5	ASTMD790	88.0	Mpa
Tensile Strength	Yield4	ASTMD638	58.0	Mpa
	Tensile Strength	Yield	ISO527-2/50	55.0	Mpa
		Tensile Strength	Break4	ASTMD638	61.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO527-2/50	60.0	Mpa
Tensile Modulus	--3	ASTMD638	2100	Mpa
Tensile Modulus	Tensile Modulus	--	ISO527-2/1	2100	Mpa
Tensile Elongation	Break	ISO527-2/50	130	%
	Tensile Elongation	Yield4	ASTMD638	6.0	%
		Tensile Elongation	Yield	ISO527-2/50	6.0	%
		Tensile Elongation	Tensile Elongation	Break4	ASTMD638	130	%
Flexural Modulus	50.0mmSpan5	ASTMD790	2070	Mpa
Flexural Modulus	Flexural Modulus	--6	ISO178	2200	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed,3.20mm	ASTMD648	134	°C
	Deflection Temperature Under Load?	0.45MPa,Unannealed,100mmSpan12	ISO75-2/Be	135	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed,3.20mm	ASTMD648	120	°C
			Deflection Temperature Under Load?	1.8MPa,Unannealed,6.40mm	ASTMD648	124	°C
			Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed,100mmSpan12	ISO75-2/Ae	124	°C
RTIElec		UL746	125	°C
Evolution Calendar intelligent importer		UL746	115	°C
Vicat Softening Temperature	--	ASTMD152513,ISO306/B12013	142	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B50	140	°C
Linear thermal expansion coefficient	MD:-40to40°C	ASTME831	6.7E-05	cm/cm/°C
	Linear thermal expansion coefficient	MD:23to80°C	ISO11359-2	7.2E-05	cm/cm/°C
		Linear thermal expansion coefficient	TD:-40to40°C	ASTME831	6.7E-05	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD:23to80°C	ISO11359-2	7.7E-05	cm/cm/°C
RTI		UL746	120	°C
Ball PressureTest	125°C	IEC60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index	CTI	UL746	PLC3
Hot-wire Ignition	HWI	UL746	PLC1
High Amp Arc Ignition	HAI	UL746	PLC0
Dielectric Strength	3.20mm,inOil	ASTMD149	17	KV/mm
Dielectric Strength	Dielectric Strength	3.20mm,in Oil	IEC60243-1	16	KV/mm
Comparative Tracking Index		IEC60112	225	V
Dissipation Factor?	50Hz	ASTMD150	2.4E-03
	Dissipation Factor?	60Hz	ASTMD150	2.4E-03
		Dissipation Factor?	1MHz	ASTMD150,IEC60250	8.5E-03
			Dissipation Factor?	50Hz	IEC60250	1E-03
			Dissipation Factor?	Dissipation Factor?	60Hz	IEC60250	1E-03
Surface Resistivity		IEC60093	>1.0E+15	ohms
Volume Resistivity		IEC60093	>1.0E+15	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	23°C11	内部方法	1100	J/m
	Unnotched Izod Impact Strength	-30°C9	ISO180/1U	无断裂
	Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C9	ISO180/1U	无断裂
Charpy Notched Impact Strength	-30°C	ISO179/1eA	60	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	75	kJ/m²
Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	52.0	J
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	无断裂
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness	H358/30	ISO2039-1	90.0	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Ignition Temperature	1.0mm	IEC60695-2-13	825	°C
Oxygen Index		ISO4589-2	35	%
UL flame retardant rating	0.8mm	UL94	V-1
	UL flame retardant rating	1.5mm	UL94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	5VA
Glow Wire Flammability Index	1.0mm	IEC60695-2-12	960	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.