PC LEXAN™ HPS6 SABIC INNOVATIVE US
87
- Unit Price:
- $8915 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:medicine medical care
- Color:--
- Grade:Light diffusion level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：--2 | 内部方法 | 0.50to0.70 | % |
| MD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| TD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Moisture Absorption | 24hr | ASTMD570 | 0.15 | % |
| Saturation,23°C | ISO62 | 0.35 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 7.0 | g/10min |
| 300°C/5.0kg | ASTMD1238 | 110 | g/10min | |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 6.50 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | Break | ASTMD638 | 140 | % |
| Yield | ASTMD638 | 6.5 | % | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 2340 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 97.9 | Mpa |
| Tensile Strength | Yield | ASTMD638 | 62.1 | Mpa |
| Flexural Strength | ISO178 | 95.0 | Mpa | |
| Tensile Modulus | ASTMD638 | 2310 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 68.9 | Mpa |
| Flexural Modulus | ISO178 | 2250 | Mpa | |
| Tensile Stress | Yield | ISO527-2/50 | 60.0 | Mpa |
| Break | ISO527-2/50 | 75.0 | Mpa | |
| Tensile Strain | Yield | ISO527-2/50 | 6.0 | % |
| Break | ISO527-2/50 | 140 | % | |
| Tensile Modulus | ISO527-2/1 | 2300 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 138 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 124 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 132 | °C | |
| 0.45MPa,Unannealed,3.20mm | ASTMD648 | 135 | °C | |
| Vicat Softening Temperature | ASTMD152511 | 154 | °C | |
| -- | ISO306/B50 | 143 | °C | |
| -- | ISO306/B120 | 140 | °C | |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 6.2E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 6E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 5.7E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 6E-05 | cm/cm/°C | |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 124 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 65.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 65.0 | J | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 15 | kJ/m² |
| 23°C | ISO179/1eA | 75 | kJ/m² | |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 | kJ/m² |
| 23°C | ISO180/1A | 70 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 118 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.