Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow	内部方法	0.50 到 0.70	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow	内部方法	0.50 到 0.70	%
Moisture Absorption	24 hr, 23°C	ISO 62	0.20	%
Melt Mass-Flow Rate	300°C/1.2 kg	ISO 1133	4.0	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	4.00	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Yield	ISO 527-2	60.0	Mpa
Tensile Strain	Break	ISO 527-2	110	%
Tensile Modulus		ISO 527-2	2300	Mpa
Flexural Modulus		ISO 178	2300	Mpa
Flexural Stress		ISO 178	92.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/Af	130	°C
Linear thermal expansion coefficient	Flow	ISO 11359-2	7.0E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow	ISO 11359-2	7.0E-5	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation Factor?	2.00 mm, 100 Hz	IEC 60250	1.0E-3
Dissipation Factor?	Dissipation Factor?	2.00 mm, 1 MHz	IEC 60250	0.090
Surface Resistivity		IEC 60093	> 1.0E+15	ohms
Volume Resistivity		IEC 60093	3.0E+16	ohms·cm
Dielectric Strength	1.00 mm	IEC 60243-1	31	KV/mm
Relative Permittivity	2.00 mm, 100 Hz	IEC 60250	3.00
Relative Permittivity	Relative Permittivity	2.00 mm, 1 MHz	IEC 60250	3.00
Comparative Tracking Index		IEC 60112	250	V

Injection	Test Result	Unit
Drying Temperature	125	°C
Mold Temperature	70 到 100	°C
Drying Time	4.0 到 6.0	hr
Rear Temperature	280 到 300	°C
Middle Temperature	290 到 310	°C
Front Temperature	310 到 330	°C
Nozzle Temperature	310 到 330	°C
Screw Speed	60 到 100	rpm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	23°C	ISO 179	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R -Sale	ISO 2039-2	118

optical performance	Test Condition	Test Method	Test Result	Unit
Transmittance	2000 µm	ISO 13468	89.0	%
Haze	2000 µm	ISO 14782	0.40	%
Refractive index of light		ISO 489	1.585

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.5 mm	UL 94	HB
	Flame Rating	3.0 mm	UL 94	HB
		Flame Rating	0.44 mm	UL 94	V-2
		Flame Rating	Flame Rating	0.75 mm	UL 94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.