PC Makrolon® 1095 000000 COVESTRO GERMANY

Unit Price:
$8073 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Low viscosity Filler: Glass fiber reinf 15% filler by weight
Application Areas:Electrical applications Power/Other Tools Industrial applications Automotive Applications Shell
Color:--
Grade:Injection grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD:2.00mm	ISO294-4	0.45	%
Shrinkage rate	Shrinkage rate	MD:2.00mm	ISO294-4	0.45	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.10	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO62	0.24	%
Melt mass flow rate	300°C/1.2kg	ISO1133	7.0	g/10min
Apparent density		ISO60	0.64	g/cm³
Melt volume flow rate	300°C/1.2kg	ISO1133	6.00	cm3/10min

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending strain 5	23°C	ISO178	5.8	%
Bending stress 4	23°C	ISO178	105	Mpa
Bending stress 4	Bending stress 4	3.5%Strain,23°C	ISO178	95.0	Mpa
Bending modulus 4	23°C	ISO178	4400	Mpa
Tensile stress	Break,23°C	ISO527-2/5	45.0	Mpa
Tensile stress	Tensile stress	Yield,23°C	ISO527-2/5	64.0	Mpa
Tensile strain	Yield,23°C	ISO527-2/5	4.6	%
Tensile strain	Tensile strain	Break,23°C	ISO527-2/5	12	%
Tensile modulus	23°C	ISO527-2/1	4600	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	135	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	141	°C
RTIElec	1.5mm	UL746	80.0	°C
Evolution Calendar intelligent importer	1.5mm	UL746	80.0	°C
RTIStr	1.5mm	UL746	80.0	°C
Vicat softening temperature	--	ISO306/B120	145	°C
Vicat softening temperature	Vicat softening temperature	--	ISO306/B50	142	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO11359-2	3.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO11359-2	6.5E-05	cm/cm/°C
BallPressure Test	136°C	IEC60695-10-2	Pass

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength	23°C,1.00mm	IEC60243-1	38	KV/mm
Relative permittivity	23°C,1MHz	IEC60250	3.20
Relative permittivity	Relative permittivity	23°C,100Hz	IEC60250	3.20
Leakage Trace Index	SolutionA	IEC60112	175	V
Leakage Trace Index	Leakage Trace Index	SolutionB	IEC60112	125	V
Dissipation factor	23°C,100Hz	IEC60250	1E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC60250	9E-03
Surface resistivity		IEC60093	1E+16	ohms
Volume resistivity	23°C	IEC60093	1E+16	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C,Complete Break	ISO179/1eU	120	kJ/m²
	Impact strength of simply supported beam without notch	-30°C,Complete Break	ISO179/1eU	100	kJ/m²
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-60°C,CompleteBreak	ISO179/1eU	90	kJ/m²
CharpyNotchedImpactStrength6	23°C,CompleteBreak	ISO7391	10	kJ/m²
NotchedIzodImpactStrength7	23°C,CompleteBreak	ISO7391	10	kJ/m²
Multi axis Instrumented Peak Impact Force	-30°C	ISO6603-2	3000	N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23°C	ISO6603-2	3600	N
Multi axis Instrumented Impact Energy	-30°C	ISO6603-2	13.0	J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO6603-2	25.0	J

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO2039-1	129	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	V-2
UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	V-0
Burning wire flammability index	1.5mm	IEC60695-2-12	960	°C
	Burning wire flammability index	0.75mm	IEC60695-2-12	850	°C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC60695-2-12	960	°C
Extreme Oxygen Index 8		ISO4589-2	27	%
Hot filament ignition temperature	1.5mm	IEC60695-2-13	900	°C
	Hot filament ignition temperature	3.0mm	IEC60695-2-13	900	°C
	Hot filament ignition temperature	Hot filament ignition temperature	0.75mm	IEC60695-2-13	850	°C
Burning rate - US-FMVSS	>1.00mm	ISO3795	passed
FlashIgnitionTemperature		ASTMD1929	470	°C
Needle flame test	MethodF:2.00mm	IEC60695-11-5	2.0	min
	Needle flame test	MethodF:1.50mm	IEC60695-11-5	2.0	min
		Needle flame test	MethodK:2.00mm	IEC60695-11-5	1.0	min
			Needle flame test	MethodK:1.50mm	IEC60695-11-5	1.0	min
				Needle flame test	MethodK:3.00mm	IEC60695-11-5	2.0	min
				Needle flame test	Needle flame test	MethodF:3.00mm	IEC60695-11-5	2.0	min
SelfIgnition		ASTMD1929	550	°C

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ISO Shortcut			ISO7391-PC,MR,(,,)-09-9,GF15
ElectrolyticalCorrosion	23°C	IEC60426	A1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.