Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD | 内部方法 | 0.64 | % |
| Modeling Shrinkage | TD | 内部方法 | 0.68 | % |
| Melt Volume flow Rate | 300°C/5.0kg | ISO1133 | 16.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| yield | | ISO527-2/5 | 58.0 | Mpa |
| fracture | | ISO527-2/5 | 47.0 | Mpa |
| fracture | | ISO527-2/5 | 17 | % |
| Break | | ASTMD638 | 19 | % |
| Flexural Modulus | | ISO178 | 2550 | Mpa |
| Break | | ASTMD638 | 47.0 | Mpa |
| Flexural Stress | --8 | ISO178 | 92.0 | Mpa |
| Flexural Stress | --9 | ISO178 | 90.0 | Mpa |
| --2 | | ASTMD638 | 2570 | Mpa |
| Yield | | ASTMD638 | 58.0 | Mpa |
| Flexural Strain (Break) | | ISO178 | 7.8 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ISO306/A50,ASTMD152517 | 144 | °C |
| 1.8MPa, Unannealed,64.0mm Span | | ISO75-2/Af | 126 | °C |
| 1.8MPa, Unannealed,3.20mm | | ASTMD648 | 111 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | ASTMD257 | 4.8E+07 | ohms |
| Volume Resistivity | | ASTMD257 | 1.4E+07 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| 23°C | | ASTMD256 | 360 | J/m |
| 23°C | | ASTMD4812 | 2100 | J/m |
| 0°C | | ASTMD256 | 290 | J/m |
| 23°C,EnergyatPeakLoad | | ASTMD3763 | 27.0 | J |
| -- | | ISO6603-2 | 63.1 | J |
| 23°C,TotalEnergy | | ASTMD3763 | 39.1 | J |
| 0°C13 | | ISO180/1A | 20 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 26 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 95 | kJ/m² |
| 23°C14 | | ISO180/1A | 25 | kJ/m² |
| 23°C15 | | ISO180/1U | 130 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.