PC Makrolon® 6267 X COVESTRO SHANGHAI
104
- Unit Price:
- $3559 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low viscosity Flame retardant
- Application Areas:Electronic and electrical Home appliance components Fitness equipment Lighting applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO2577 | 0.50到0.70 | % |
| MD | ISO2577 | 0.50到0.70 | % | |
| TD:2.00mm4 | ISO294-4 | 0.65 | % | |
| MD:2.00mm4 | ISO294-4 | 0.65 | % | |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
| Melt Mass-Flow Rate | 300°C/1.2kg | ISO1133 | 20 | g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 19.0 | cm3/10min |
| Apparent Density | ISO60 | 0.64 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Strain | 23°C | ISO178 | 6.9 | % |
| Flexural Modulus | 23°C | ISO178 | 2400 | Mpa |
| Flexural Stress | 23°C | ISO178 | 97.0 | Mpa |
| 3.5%Strain,23°C | ISO178 | 74.0 | Mpa | |
| Nominal Tensile Strain at Break | 23°C | ISO527-2/50 | >50 | % |
| Tensile Stress | Yield,23°C | ISO527-2/50 | 67.0 | Mpa |
| Break,23°C | ISO527-2/50 | 65.0 | Mpa | |
| Tensile Strain | Yield,23°C | ISO527-2/50 | 6.0 | % |
| Break,23°C | ISO527-2/50 | 120 | % | |
| Tensile Modulus | 23°C | ISO527-2/1 | 2450 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 134 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 122 | °C | |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 | °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 144 | °C |
| -- | ISO306/B120 | 145 | °C | |
| Linear thermal expansion coefficient | MD:23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD:23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| Thermal Conductivity | 23°C | ISO8302 | 0.20 | W/m/K |
| RTI | 1.5mm | UL746 | 125 | °C |
| Ball PressureTest | 135°C | IEC60695-10-2 | 通过 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| Relative Permittivity | 23°C,100Hz | IEC60250 | 3.10 | |
| 23°C,1MHz | IEC60250 | 3.00 | ||
| Comparative Tracking Index | SolutionA | IEC60112 | 225 | V |
| SolutionB | IEC60112 | 125 | V | |
| Dissipation Factor? | 23°C,100Hz | IEC60250 | 8E-04 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| Surface Resistivity | IEC60093 | 1E+16 | ohms | |
| Volume Resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 | |
| 23°C | ISO179/1eU | 无断裂 | ||
| Multi-Axial Instrumented Impact Energy | -30°C | ISO6603-2 | 55.0 | J |
| 23°C | ISO6603-2 | 50.0 | J | |
| Charpy Notched Impact Strength | -30°C,Complete Break | ISO7391 | 12 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 60 | kJ/m² | |
| Notched Izod Impact Strength | -30°C,Complete Break | ISO7391 | 11 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 15 | kJ/m² | |
| Multi-Axial Instrumented Impact Peak Force | -30°C | ISO6603-2 | 5900 | N |
| 23°C | ISO6603-2 | 5000 | N |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball Indentation Hardness | ISO2039-1 | 116 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| Glow Wire Flammability Index | 0.75mm | IEC60695-2-12 | 960 | °C |
| 1.5mm | IEC60695-2-12 | 960 | °C | |
| 3.0mm | IEC60695-2-12 | 960 | °C | |
| ApplicationofFlamefromSmallBurner MethodKandF | 2.00mm | DIN53438-1,-3 | K1,F1 | |
| NeedleFlameTest | MethodF:1.50mm | IEC60695-11-5 | 2.0 | min |
| MethodF:2.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodF:3.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodK:1.50mm | IEC60695-11-5 | 2.0 | min | |
| MethodK:2.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodK:3.00mm | IEC60695-11-5 | 2.0 | min | |
| FMVSS Flammability | >1.00mm | ISO3795 | passed | |
| FlashIgnition | ASTMD1929 | 460 | °C | |
| Oxygen Index | ISO4589-2 | 36 | % | |
| SelfIgnition | ASTMD1929 | 530 | °C |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortname | ISO7391-PC,MFLR,(,, | |||
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.