PC PANLITE® ML-5206ZLP TEIJIN JAPAN
75
- Unit Price:
- $4831 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 56MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability transparent
- Application Areas:Electrical tools Lighting fixtures
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD | In-house method | 0.5-0.7 | % |
| TD | In-house method | 0.5-0.7 | % | |
| TD:4.00mm | 内部方法 | 0.50到0.70 | % | |
| MD:4.00mm | 内部方法 | 0.50到0.70 | % | |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.20 | % |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 3.50 | cm3/10min |
| Melt Mass-Flow Rate | 300℃ | ISO 1133 | 3.5 | cm310min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength(Break) | 50mm/min | ISO 527-1 | 53 | Mpa |
| Tensile Strength(Yield) | 50mm/min | ISO 527-1,2 | 65 | Mpa |
| Nominal Tensile Strain at Break | ISO527-2/50 | 25 | % | |
| Flexural Modulus | ISO178 | 2400 | Mpa | |
| Flexural Stress | ISO178 | 98.0 | Mpa | |
| Tensile Stress | Yield | ISO527-2/50 | 65.0 | Mpa |
| Break | ISO527-2/50 | 53.0 | Mpa | |
| Tensile Strain | Yield | ISO527-2/50 | 6.0 | % |
| Notched Impact Strength | Notched | ISO 179 | 8.0 | kJ/m² |
| Tensile Elongation?(Break) | 50mm/min | ISO 527-1 | 25 | % |
| Tensile Modulus | ISO527-2/1 | 2400 | Mpa | |
| Flexural Modulus | 2mm/min | ISO 178 | 2400 | Mpa |
| Flexural Strength | 2mm/min | ISO 178 | 98 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 122 | °C |
| 1.80MPa | ISO 75-1,2 | 122 | °C | |
| 线膨胀系数，MD | ISO 11359-2 | 0.7 | X10-4/℃ | |
| TD | ISO 11359-2 | 0.7 | X10-4/℃ | |
| Flame retardancy | 1.5mmt | UL94 | V-0 | |
| RTIElec | 1.5mm | UL746 | 130 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 125 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| TD | ISO11359-2 | 7E-05 | cm/cm/°C | |
| RTI | 1.5mm | UL746 | 130 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Comparative Tracking Index | IEC60112 | 250 | V | |
| Surface Resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 无断裂 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Transmittance | 1.5mmt | JIS K7136 | 85 | % |
| Transmittance | 3000µm | ASTMD1003 | 77.0 | % |
| Particle Size Distribution | 2.0mmt | In-house method | 17 | % |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| Glow Wire Flammability Index | 1.5mm | IEC60695-2-12 | 960 | °C |
| 3.0mm | IEC60695-2-12 | 960 | °C | |
| Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 875 | °C |
| 3.0mm | IEC60695-2-13 | 875 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.