PC LEXAN™ FXE1414L WH9D155 SABIC INNOVATIVE NANSHA

Unit Price:
$4492 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10.3MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Low temperature resistanc transparent Flame retardant
Application Areas:Electrical field Electrical appliances Electronic field Household appliances
Color:--
Grade:Light diffusion level

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD：3.20mm	内部方法	0.40to0.80	%
Moisture Absorption	Saturation, 23°C	ISO 62	0.17	%
	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.070	%
		Moisture Absorption	Saturation,23°C	ISO62	0.35	%
		Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.15	%
Melt Mass-Flow Rate	300°C/1.2kg	ASTMD1238	10	g/10min
Melt Volume flow Rate	300°C/1.2kg	ISO1133	9.00	cm3/10min
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	11	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	10.0	cm3/10min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.40 到 0.80	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	-- 5, 6	ISO 178	83.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	86.0	Mpa
Tensile Elongation	Break	ASTMD638	98	%
Flexural Modulus		ISO178	2250	Mpa
Tensile Elongation	Yield	ASTMD638	6.0	%
Tensile Modulus		ASTMD638	2020	Mpa
Tensile Strength	Yield	ASTMD638	55.5	Mpa
Tensile Strength	Tensile Strength	Break	ASTMD638	50.3	Mpa
Flexural Modulus	50.0mmSpan	ASTMD790	2230	Mpa
Flexural Strength	Yield,50.0mmSpan	ASTMD790	92.4	Mpa
Flexural Strength		ISO178	85.0	Mpa
Tensile Stress	Yield	ISO527-2/50	57.0	Mpa
Tensile Stress	Tensile Stress	Break	ISO527-2/50	60.0	Mpa
Tensile Strain	Break	ISO527-2/50	120	%
Tensile Strain	Tensile Strain	Yield	ISO527-2/50	6.0	%
Tensile Modulus	-- 2	ASTM D638	2030	Mpa
	Tensile Modulus	--	ISO 527-2/1	2000	Mpa
	Tensile Modulus	Tensile Modulus		ISO527-2/1	2150	Mpa
Tensile Elongation	Yield 3	ASTM D638	5.0	%
	Tensile Elongation	Yield	ISO 527-2/50	5.0	%
		Tensile Elongation	Break 3	ASTM D638	84	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	75	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2050	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2110	Mpa
Tensile Strength	Yield 3	ASTM D638	52.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	52.0	Mpa
		Tensile Strength	Break 3	ASTM D638	54.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	47.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature		ASTMD152510	145	°C
	Vicat Softening Temperature	--	ISO306/B50	145	°C
		Vicat Softening Temperature	--	ISO306/B120	146	°C
			Vicat Softening Temperature	--	ASTM D15259, ISO 306/B509	138	°C
			Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	146	°C
Deflection Temperature Under Load?	0.45MPa,Unannealed,3.20mm	ASTMD648	139	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed,3.20mm	ASTMD648	124	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831, ISO 11359-2	7.0E-5	cm/cm/°C
	Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	6.7E-5	cm/cm/°C
		Linear thermal expansion coefficient	Across Flow : -40°C	ISO 11359-2	8.2E-5	cm/cm/°C
			Linear thermal expansion coefficient	MD：-40to40°C	ASTME831	7E-05	cm/cm/°C
				Linear thermal expansion coefficient	MD：23to80°C	ISO11359-2	7.2E-05	cm/cm/°C
					Linear thermal expansion coefficient	TD：-40to40°C	ASTME831	7.5E-05	cm/cm/°C
					Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：23to80°C	ISO11359-2	7.2E-05	cm/cm/°C
Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	121	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8	ISO 75-2/Af	118	°C
Heat Deflection Temperature	1.8MPa,Unannealed,100mmSpan	ISO75-2/Ae	128	°C

Injection	Test Result	Unit
Drying Time	3.0 到 4.0	hr
Rear Temperature	260 到 280	°C
Middle Temperature	280 到 305	°C
Front Temperature	295 到 315	°C
Nozzle Temperature	290 到 310	°C
Hopper Temperature	60 到 80	°C
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	295 到 315	°C
Mold Temperature	70 到 95	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	-30°C	ISO180/1U	NoBreak
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C	ISO180/1U	NoBreak
Charpy Notched Impact Strength	-30°C	ISO179/1eA	65	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	70	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	NoBreak
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	NoBreak
Notched Izod Impact Strength	-30°C	ISO180/1A	60	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	70	kJ/m²
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	68.0	J
Instrumented Dart Impact	Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	70.0	J

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.40 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.