Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.40to0.60 | % |
Modeling Shrinkage | MD:4.00mm | 内部方法 | 0.40to0.60 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.14 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO527-2/5 | 55.0 | Mpa |
Tensile Strain | Break | ISO527-2/5 | 30 | % |
Tensile Modulus | | ISO527-2/1 | 3250 | Mpa |
Flexural Modulus | | ISO178 | 3200 | Mpa |
Flexural Stress | | ISO178 | 93.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
RTIElec | 1.5mm | UL746 | 130 | °C |
Evolution Calendar intelligent importer | 1.5mm | UL746 | 125 | °C |
RTIStr | 1.5mm | UL746 | 130 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 137 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 127 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 6E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 6E-05 | cm/cm/°C |
Vicat Softening Temperature | | ISO306/B50 | 141 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Dissipation Factor? | 100Hz | IEC60250 | 1E-03 | |
Dissipation Factor? | 1MHz | IEC60250 | 9E-03 | |
Relative Permittivity | 100Hz | IEC60250 | 3.40 | |
Relative Permittivity | 1MHz | IEC60250 | 3.40 | |
Comparative Tracking Index | | IEC60112 | 175 | V |
Dielectric Strength | | IEC60243-1 | 35 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | | ISO179 | 60 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.8mm | UL94 | V-2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.