Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | % | ISO 294-4 | 0.65-0.7 |
Melt index | | g/10min | ISO 1133 | |
Moisture Absorption | | % | ISO 62 | 0.12 |
Density / Specific Gravity | | g/cm | ISO 1183 | 1.2 |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Yield tensile strain | | % | ISO 527-2 | 6.1 |
Tensile Strength(Break) | | MPa | ISO 527-2 | |
Tensile Strength(Yield) | | MPa | ISO 527-2 | 66 |
Breaking tensile strain | | % | ISO 527-2 | |
IZOD Notch Impact Strength | 23℃ | KJ/m | ISO 180/1A | 85 |
Tensile Modulus | | MPa | ISO 527-2 | 2400 |
Flexural Modulus | | MPa | ISO 178 | 2400 |
Flexural Strength | | MPa | ISO 178 | 73 |
Charpy Notched Impact Strength | 23℃ | KJ/m | ISO 179/1eA | 75 |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flame retardancy | -,2.5mm | | UL94 | HB |
Flame retardancy | -,3.00mm | | UL94 | HB |
Flame retardancy | -,6.00mm | | UL94 | HB |
Flame retardancy | -,0.75mm | | UL94 | V-2 |
Flame retardancy | -,1.50mm | | UL94 | V-2 |
Flame retardancy | -,2.4mm | | UL94 | V-2 |
Deflection Temperature Under Load? | -,0.45Mpa | ℃ | ISO 75-2 | |
Deflection Temperature Under Load? | -,1.8Mpa | ℃ | ISO 75-2 | |
Vicat Softening Temperature | | ℃ | ISO 306 | |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | kV/mm | IEC 60243-1 | 34 |
Surface Resistivity | | Ohm | IEC 60093 | |
Volume Resistivity | | Ohm.m | IEC 60093 | |
Relative Permittivity | -,100Hz | | IEC 60250 | 3.1 |
Relative Permittivity | -,1MHz | | IEC 60250 | |
Other | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | % | ISO 4589-2 | 27 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.