PC LNP™ LUBRILOY™ D2000 BK1A643 SABIC INNOVATIVE US

Unit Price:
$4975 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:wear resistant
Application Areas:Electrical appliances Electronic display Aerospace Applications
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 24hr	ASTM D955	0.70 到 0.90	%
	Modeling Shrinkage	Across Flow : 24hr	ASTM D955	0.70 到 0.90	%
		Modeling Shrinkage	Across Flow : 24hr	ISO 294-4	0.70 到 0.90	%
		Modeling Shrinkage	Modeling Shrinkage	流量 : 24hr	ISO 294-4	0.70 到 0.90	%
Moisture Absorption	24 hr, 50% RH	ASTM D570	0.14	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.18	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus	-- 2	ASTM D638	1860	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2120	Mpa
Tensile Elongation	Yield	ASTM D638	6.5	%
	Tensile Elongation	Yield	ISO 527-2	5.6	%
		Tensile Elongation	Break	ASTM D638	130	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2	99	%
Flexural Modulus		ASTM D790, ISO 178	2130	Mpa
Flexural Strength	--	ASTM D790	82.0	Mpa
Flexural Strength	Flexural Strength	--	ISO 178	78.0	Mpa
Tensile Strength	Yield	ASTM D638	53.0	Mpa
	Tensile Strength	Yield	ISO 527-2	51.0	Mpa
		Tensile Strength	Break	ASTM D638	60.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2	54.0	Mpa
Coefficient of Friction	Dynamic	ASTM D3702	0.16
Coefficient of Friction	Coefficient of Friction	Static	ASTM D3702	0.090
Specific Wear Rate		ASTM D3702	1.2E+7	10^-8 mm³/N·m

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	142	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 4	ISO 75-2/Bf	140	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	130	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 4	ISO 75-2/Af	128	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831, ISO 11359-2	7.4E-5	cm/cm/°C
	Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	7.4E-5	cm/cm/°C
	Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -40°C	ISO 11359-2	7.4E-5	cm/cm/°C

Injection	Test Result	Unit
Drying Temperature	100	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	305 到 315	°C
Mold Temperature	65 到 95	°C
Drying Time	4.0	hr
Rear Temperature	295 到 305	°C
Middle Temperature	300 到 310	°C
Front Temperature	305 到 315	°C
Back Pressure	0.200 到 0.300	Mpa
Screw Speed	30 到 60	rpm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C, Energy at Peak	ASTM D3763	40.0	J
Instrumented Dart Impact	Instrumented Dart Impact	--	ISO 6603-2	45.0	J
Unnotched Izod Impact Strength	23°C	ASTM D4812	无断裂
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C 4	ISO 180/1U	140	kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.