Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility Flame retardant
Application Areas:Non specific food
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Method	Test Result	Unit
Density	ASTM D792/ISO 1183	1.19
Modeling Shrinkage	ASTM D955	0.5 - 0.7	%
Moisture Absorption 23℃/24H	ASTM D570/ISO 62	0.24	%

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD:3.20mm		0.50to0.70	%
	Modeling Shrinkage	MD:3.20mm		0.50to0.70	%
	Modeling Shrinkage	Modeling Shrinkage	吸水率(Saturation,23°C)		0.24	%
Melt Mass-Flow Rate	300°C/1.2kg	ISO1133	22	g/10min
Melt Volume flow Rate	300°C/1.2kg	ISO1133	21.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress		ISO178	92.0	Mpa
Tensile Stress	Yield	ISO527-2	61.0	Mpa
Tensile Strain	Yield	ISO527-2	4.7	%
Tensile Modulus		ASTM D638/ISO 527	2300	kg/cm²(MPa)[Lb/in²]
Tensile Modulus	Tensile Modulus		ISO527-2	2300	Mpa
Flexural Modulus		ASTM D790/ISO 178	2500	kg/cm²(MPa)[Lb/in²]
Flexural Modulus	Flexural Modulus		ISO178	2500	Mpa
Flexural Strength		ASTM D790/ISO 178	92	kg/cm²(MPa)[Lb/in²]
Nominal Tensile Strain at Break		ISO527-2	67	%
Tensile Elongation?(Break)		ASTM D638/ISO 527	67	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Burning Rate		UL94	V-0 (1.0mm)
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	137	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	125	°C
Linear expansion coefficient		ASTM D696/ISO 11359	6.6E-05	mm/mm.℃
Linear thermal expansion coefficient	MD	ISO11359-2	6.6E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	6.7E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation Factor?	100Hz	IEC60250	6E-04
Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	9E-03
Dielectric Strength	1.00mm	IEC60243-1	31	KV/mm
Dielectric Strength	Dielectric Strength	3.00mm	IEC60243-1	18	KV/mm
Relative Permittivity	100Hz	IEC60250	3.10
Relative Permittivity	Relative Permittivity	1MHz	IEC60250	3.10
Surface Resistivity		IEC60093	6E+15	ohms
Surface Resistivity	Surface Resistivity		ASTM D257/IEC 60093	6.E+15	Ω
Dielectric Constant		ASTM D150/IEC 60250	3.1
Volume Resistivity		ASTM D257/IEC 60093	3.E+14	Ω.cm
Volume Resistivity	Volume Resistivity		IEC60093	3E+16	ohms·cm

Processing	Test Condition	Test Method	Test Result	Unit
Drying conditions			热风干燥 120℃---約4-8小时
Screw Speed			50-100	rpm
Mold Temperature			70-100	°C
Processing temperature			250-280	°C
	Processing temperature			270-300	°C
	Processing temperature	Processing temperature			260-290	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	23°C	ISO179	NoBreak

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.0mm	UL94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.