PC Makrolon® 6487 COVESTRO GERMANY
56
- Unit Price:
- $3169 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | TD | ISO2577 | 0.60to0.80 | % |
MD | ISO2577 | 0.60to0.80 | % | |
TD:2.00mm3 | ISO294-4 | 0.75 | % | |
MD:2.00mm3 | ISO294-4 | 0.70 | % | |
Moisture Absorption | Saturation,23°C | ISO62 | 0.30 | % |
Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
Melt Mass-Flow Rate | 300°C/1.2kg | ISO1133 | 10 | g/10min |
Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
Density / Specific Gravity | 23°C | ISO1183 | 1.20 | g/cm³ |
Apparent Density | ISO60 | 0.64 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Nominal Tensile Strain at Break | 23°C | ISO527-2/50 | >50 | % |
Flexural Strain | 23°C | ISO178 | 7.0 | % |
Flexural Stress | 3.5%Strain,23°C | ISO178 | 75.0 | Mpa |
23°C | ISO178 | 99.0 | Mpa | |
Flexural Modulus | 23°C | ISO178 | 2450 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2/50 | 66.0 | Mpa |
Break,23°C | ISO527-2/50 | 65.0 | Mpa | |
Tensile Strain | Yield,23°C | ISO527-2/50 | 6.0 | % |
Break,23°C | ISO527-2/50 | 120 | % | |
Tensile Modulus | 23°C | ISO527-2/1 | 2450 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 134 | °C |
1.8MPa,Unannealed | ISO75-2/A | 122 | °C | |
RTIElec | 1.5mm | UL746 | 125 | °C |
Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 | °C |
RTIStr | 1.5mm | UL746 | 125 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 143 | °C |
-- | ISO306/B120 | 141 | °C | |
Linear thermal expansion coefficient | MD:23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
TD:23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
Glass Transition Temperature | ISO11357-2 | 141 | °C | |
Thermal Conductivity | 23°C | ISO8302 | 0.20 | W/m/K |
Ball PressureTest | 135°C | IEC60695-10-2 | Pass |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Dielectric Strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
Relative Permittivity | 23°C,100Hz | IEC60250 | 3.10 | |
23°C,1MHz | IEC60250 | 3.00 | ||
Comparative Tracking Index | SolutionA | IEC60112 | 225 | V |
SolutionB | IEC60112 | 125 | V | |
Dissipation Factor? | 23°C,100Hz | IEC60250 | 8E-04 | |
23°C,1MHz | IEC60250 | 9E-03 | ||
Surface Resistivity | IEC60093 | 1E+16 | ohms | |
Volume Resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
23°C | ISO179/1eU | NoBreak | ||
Multi-Axial Instrumented Impact Energy | -30°C | ISO6603-2 | 55.0 | J |
23°C | ISO6603-2 | 50.0 | J | |
Notched Izod Impact Strength | -30°C,Complete Break | ISO7391 | 12 | kJ/m² |
23°C,Partial Break | ISO7391 | 65 | kJ/m² | |
Multi-Axial Instrumented Impact Peak Force | -30°C | ISO6603-2 | 6000 | N |
23°C | ISO6603-2 | 5200 | N | |
Charpy Notched Impact Strength | -30°C,Complete Break | ISO7391 | 12 | kJ/m² |
23°C,Partial Break | ISO7391 | 70 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Ball Indentation Hardness | ISO2039-1 | 117 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
UL flame retardant rating | 1.5mm | UL94 | V-0 | |
3.0mm | UL94 | 5VA | ||
Glow Wire Flammability Index | 1.5mm | IEC60695-2-12 | 960 | °C |
3.0mm | IEC60695-2-12 | 960 | °C | |
Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 900 | °C |
3.0mm | IEC60695-2-13 | 930 | °C | |
FMVSS Flammability | >1.00mm | ISO3795 | passed | |
FlashIgnition | ASTMD1929 | 470 | °C | |
Oxygen Index | ISO4589-2 | 36 | % | |
SelfIgnition | ASTMD1929 | 550 | °C | |
ApplicationofFlamefromSmallBurner MethodKandF | 2.00mm | DIN53438-1,-3 | K1,F1 |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
ISO Shortname | ISO7391-PC,MFLR,(,,)-09-9 | |||
ElectrolyticalCorrosion | 23°C | IEC60426 | A1 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.