Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | Flow | ASTM D-955 | 0.02～0.2 | % |
| Modeling Shrinkage | Across Flow | ASTM D-955 | 0.3～0.5 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Compressive Strength | | ASTM D-695 | 157(1600) | MPa(Kgf/cm |
| Tensile Modulus | | ASTM D-638 | 8240(84000) | MPa(Kgf/cm |
| Tensile Strength | | ASTM D-638 | 126(1280) | MPa(Kgf/cm |
| Tensile Elongation | Break | ASTM D-638 | 3.5 | % |
| Rockwell Hardness | | ASTM D-785 | 93 | M标度 |
| Flexural Modulus | | ASTM D-790 | 7260(74000) | MPa(Kgf/cm |
| Flexural Strength | | ASTM D-790 | 186(1900) | MPa(Kgf/cm |
| Notched Izod Impact Strength | 艾氏、带Notched厚度6.4mm | ASTM D-256 | 157(16) | J/m(kgf·cm/cm) |
| Notched Izod Impact Strength | 艾氏、带Notched厚度3.2mm | ASTM D-256 | 157(16) | J/m(kgf·cm/cm) |
| Insulation failure strength | 快速加压值厚度1.6mm | ASTM D-149 | 30 | KV/mm |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 负荷1.813MPa(18.6kgf/cm | JIS K-7207 | 149 | °C |
| Heat Deflection Temperature | 负荷0.451MPa(4.6kgf/cm | JIS K-7207 | 151 | °C |
| Temperature Index | 电学式，厚度1.47mm | UL 746B | 130 | °C |
| Temperature Index | 冲击式，厚度1.47mm | UL 746B | 125 | °C |
| Temperature Index | 非冲击式，厚度1.47mm | UL 746B | 130 | °C |
| Coefficient of Linear Thermal Expansion | Flow | ASTM D-696 | 2.0 | |
| Coefficient of Linear Thermal Expansion | Across Flow | ASTM D-696 | 5.6 | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Arc Resistance | | ASTM D-495 | 100 | sec |
| Volume Resistivity | | ASTM D-257 | 1×10 | Ω.cm |
| Dissipation Factor (Tangent) | 10 | ASTM D-150 | 0.009 | |
| Dissipation Factor (Tangent) | 60Hz | ASTM D-150 | 0.0008 | |
| Comparative Tracking Index | | IEC 112 | 180 | V |
| Dielectric Constant | 60Hz | ASTM D-150 | 3.51 | |
| Dielectric Constant | 10 | ASTM D-150 | 3.41 | |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 24hr，in 23℃ | ASTM D-570 | 0.12 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.