PC INFINO® SI-3109G K2007 BK Samsung Cheil South Korea
80
- Unit Price:
- $3249 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Carbon fiber flame retard UV resistance High gloss Filler: Glass fiber reinf
- Application Areas:Electronic and electric p Electronic and electrical Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 250°C/10.0kg | ASTMD1238 | 20 | g/10min |
| 250°C/2.16kg | ISO1133 | 19 | g/10min | |
| Ash Content | ISO3451 | 9.8 | % | |
| Modeling Shrinkage | MD：3.20mm | ASTMD955 | 0.30to0.50 | % |
| Modeling Shrinkage | ASTM D-955 | 0.3-0.5 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | ISO178 | 88.0 | Mpa | |
| IZOD Notch Impact Strength | 1/8" | ASTM D-256 | 9 | Kgf.cm/cm |
| Flexural Modulus | ISO178 | 2600 | Mpa | |
| Tensile Modulus | ASTMD638 | 2160 | Mpa | |
| Tensile Strength | Yield | ASTMD638 | 55.9 | Mpa |
| Flexural Modulus | ASTMD790 | 2450 | Mpa | |
| Flexural Strength | ASTMD790 | 88.3 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 47.1 | Mpa |
| Tensile Elongation | Break | ASTMD638 | 47 | % |
| Tensile Stress | Yield | ISO527-2/50 | 57.0 | Mpa |
| Break | ISO527-2/50 | 46.0 | Mpa | |
| Tensile Strain | Break | ISO527-2/50 | 15 | % |
| Tensile Modulus | ISO527-2/50 | 2400 | Mpa | |
| Tensile Strength | 5mm/min | ASTM D-638 | 570 | Kgf/cm |
| Rockwell Hardness | ASTM D-785 | 89 | R-Scale | |
| Flexural Modulus | 2.8mm/min | ASTM D-790 | 29000 | Kgf/cm |
| Flexural Strength | 2.8mm/min | ASTM D-790 | 1100 | Kgf/cm |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 142 | °C |
| 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 140 | °C | |
| 0.45MPa,Annealed,4.00mm | ISO75-2/B | 140 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 131 | °C | |
| 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 127 | °C | |
| 1.8MPa,Annealed,4.00mm | ISO75-2/A | 128 | °C | |
| 1/4" 18.56kgf/cm | ASTM D-648 | 120 | °C | |
| Vicat Softening Temperature | 5kg | ASTM D-1525 | N/A | °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 145146 | °C |
| -- | ISO306/B120 | 147148 | °C | |
| Flame retardancy | UL 94 | 0.8 V-2 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | 23°C | ISO180/1A | 8.9 | kJ/m² |
| CharpyNotchedImpactStrength6 | 23°C | ISO179/1eA | 10 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 89 | |
| R-Scale | ISO2039-2 | 120 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | V-2 |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | 24hrimmersion | ASTM D-570 | 0.15 | % |
| Melt index | 200℃ 5kg | ASTM D-1238 | 21.0 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.