PC LNP™ LUBRICOMP™ DFL-4534 BK SABIC INNOVATIVE US
63
- Unit Price:
- $5337 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Easy to form Easy to demould
- Application Areas:Electronic and Electrical Lighting applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow : 24hr | ASTM D955 | 0.30 到 0.50 | % |
| Across Flow : 24hr | ASTM D955 | 0.30 到 0.50 | % | |
| Across Flow : 24hr | ISO 294-4 | 0.44 | % | |
| 流量 : 24hr | ISO 294-4 | 0.36 | % | |
| Moisture Absorption | 24 hr, 50% RH | ASTM D570 | 0.10 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | -- 1 | ASTM D638 | 6890 | Mpa |
| -- | ISO 527-2/1 | 6740 | Mpa | |
| Tensile Elongation | Yield | ASTM D638 | 2.8 | % |
| Yield | ISO 527-2 | 2.5 | % | |
| Break | ASTM D638 | 2.8 | % | |
| Break | ISO 527-2 | 2.5 | % | |
| Flexural Modulus | -- | ASTM D790 | 6200 | Mpa |
| -- | ISO 178 | 6400 | Mpa | |
| Flexural Strength | ASTM D790, ISO 178 | 158 | Mpa | |
| Tensile Strength | Yield | ASTM D638, ISO 527-2 | 103 | Mpa |
| Break | ASTM D638 | 103 | Mpa | |
| Break | ISO 527-2 | 104 | Mpa | |
| Coefficient of Friction | Dynamic | ASTM D3702 | 0.51 | |
| Static | ASTM D3702 | 0.53 | ||
| Specific Wear Rate | ASTM D3702 | 2.2E+7 | 10^-8 mm³/N·m |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 143 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 3 | ISO 75-2/Bf | 145 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 141 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 3 | ISO 75-2/Af | 141 | °C | |
| Linear thermal expansion coefficient | Flow : -40 to 40°C | ASTM E831, ISO 11359-2 | 4.7E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 3.6E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 3.6E-5 | cm/cm/°C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 120 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 305 到 325 | °C | ||
| Mold Temperature | 80 到 110 | °C | ||
| Drying Time | 4.0 | hr | ||
| Rear Temperature | 295 到 305 | °C | ||
| Middle Temperature | 310 到 320 | °C | ||
| Front Temperature | 320 到 330 | °C | ||
| Back Pressure | 0.200 到 0.300 | Mpa | ||
| Screw Speed | 30 到 60 | rpm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 24.0 | J |
| -- | ISO 6603-2 | 6.00 | J | |
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 720 | J/m |
| 23°C 3 | ISO 180/1U | 44 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.