PC LEXAN™ BPL1000 BK SABIC INNOVATIVE NANSHA

Unit Price:
$4163 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
34MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:UV resistance Hydrolysis resistance
Application Areas:Thin walled products Electronic and electrical Automotive components
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD：--2	内部方法	0.50to0.70	%
	Modeling Shrinkage	MD：3.20mm	内部方法	0.50to0.70	%
	Modeling Shrinkage	Modeling Shrinkage	TD：3.20mm	内部方法	0.50to0.70	%
Moisture Absorption	Saturation,23°C	ISO62	0.35	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.15	%
Melt Mass-Flow Rate	300°C/1.2kg	ASTMD1238	25	g/10min
Melt Volume flow Rate	300°C/1.2kg	ISO1133	23.2	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	Break	ASTMD638	96	%
Tensile Elongation	Tensile Elongation	Yield	ASTMD638	4.8	%
Flexural Modulus	50.0mmSpan	ASTMD790	2670	Mpa
Flexural Strength	Yield,50.0mmSpan	ASTMD790	102	Mpa
Tensile Strength	Yield	ASTMD638	63.4	Mpa
Tensile Stress	Yield	ISO527-2/50	64.8	Mpa
Tensile Stress	Tensile Stress	Break	ISO527-2/50	53.5	Mpa
Tensile Strain	Yield	ISO527-2/50	4.7	%
Tensile Strain	Tensile Strain	Break	ISO527-2/50	97	%
Tensile Modulus		ISO527-2/1	2460	Mpa
Flexural Strength		ISO178	94.8	Mpa
Tensile Modulus		ASTMD638	2680	Mpa
Tensile Strength	Break	ASTMD638	51.0	Mpa
Flexural Modulus		ISO178	2370	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Heat Deflection Temperature	1.8MPa,Unannealed,64.0mmSpan	ISO75-2/Af	96.1	°C
Deflection Temperature Under Load?	0.45MPa,Unannealed,3.20mm	ASTMD648	106	°C
Linear thermal expansion coefficient	MD：-40to40°C	ASTME831	7E-05	cm/cm/°C
	Linear thermal expansion coefficient	MD：-40to40°C	ISO11359-2	7E-05	cm/cm/°C
		Linear thermal expansion coefficient	TD：-40to40°C	ASTME831	7E-05	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：-40to40°C	ISO11359-2	7E-05	cm/cm/°C
RTIElec		UL746	80.0	°C
Evolution Calendar intelligent importer		UL746	80.0	°C
RTIStr		UL746	80.0	°C
Vicat Softening Temperature		ASTMD152511	111	°C
	Vicat Softening Temperature	--	ISO306/B50	113	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B120	114	°C
Ball PressureTest	75°C	IEC60695-10-2	Pass

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative Permittivity	50Hz	IEC60250	3.00
	Relative Permittivity	60Hz	IEC60250	3.00
	Relative Permittivity	Relative Permittivity	1MHz	IEC60250	2.90
Comparative Tracking Index		IEC60112	200	V
Dissipation Factor?	50Hz	IEC60250	0.030
	Dissipation Factor?	60Hz	IEC60250	0.030
	Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	0.010
Dielectric Strength	1.60mm,inOil	ASTMD149	27	KV/mm
Surface Resistivity		IEC60093	>1.0E+15	ohms
Volume Resistivity		IEC60093	>1.0E+15	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	48.6	J
CharpyNotchedImpactStrength8	23°C	ISO179/1eA	18	kJ/m²
Notched Izod Impact Strength	-30°C	ISO180/1A	12	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	18	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.45mm	UL94	V-2
UL flame retardant rating	UL flame retardant rating	0.8mm	UL94	V-0
Glow Wire Flammability Index	1.0mm	IEC60695-2-12	960	°C
Oxygen Index		ISO4589-2	36	%
Glow Wire Ignition Temperature	1.0mm	IEC60695-2-13	800	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.