PC LNP™ LUBRILOY™ D20001 BK1E055 SABIC INNOVATIVE US

Unit Price:
$4669 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 24hr	ASTM D955	0.50	%
	Modeling Shrinkage	Across Flow : 24hr	ASTM D955	0.60	%
		Modeling Shrinkage	Across Flow : 24hr	ISO 294-4	0.57	%
		Modeling Shrinkage	Modeling Shrinkage	流量 : 24hr	ISO 294-4	0.53	%
Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.12	%
Melt Volume flow Rate	300°C/1.2 kg	ASTM D1238	15.7	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Coefficient of Friction	Dynamic	ASTM D3702	0.090
Coefficient of Friction	Coefficient of Friction	Static	ASTM D3702	0.22
Specific Wear Rate		ASTM D3702	6.0E+6	10^-8 mm³/N·m
Tensile Modulus	-- 2	ASTM D638	2550	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2600	Mpa
Tensile Elongation	Yield	ASTM D638	4.5	%
	Tensile Elongation	Yield	ISO 527-2	4.3	%
		Tensile Elongation	Break	ASTM D638	6.5	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2	6.7	%
Flexural Modulus	--	ASTM D790	2820	Mpa
Flexural Modulus	Flexural Modulus	--	ISO 178	2800	Mpa
Flexural Strength	--	ASTM D790	103	Mpa
Flexural Strength	Flexural Strength	--	ISO 178	102	Mpa
Tensile Strength	Yield	ASTM D638	67.0	Mpa
	Tensile Strength	Yield	ISO 527-2	62.0	Mpa
		Tensile Strength	Break	ASTM D638	60.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2	54.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831, ISO 11359-2	6.6E-5	cm/cm/°C
	Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	6.7E-5	cm/cm/°C
	Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : -40°C	ISO 11359-2	6.7E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	97.0	°C
	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	89.0	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 4	ISO 75-2/Af	94.0	°C

Injection	Test Result	Unit
Drying Time	4.0 到 6.0	hr
Rear Temperature	250 到 260	°C
Middle Temperature	255 到 265	°C
Front Temperature	260 到 270	°C
Back Pressure	0.200 到 0.300	Mpa
Screw Speed	30 到 60	rpm
Drying Temperature	80	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	255 到 290	°C
Mold Temperature	40 到 65	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	23°C	ASTM D4812	1600	J/m
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C 4	ISO 180/1U	100	kJ/m²
Instrumented Dart Impact	23°C, Energy at Peak	ASTM D3763	51.0	J

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.5 mm, Testing by SABIC	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.