PC LEXAN™ 123-111 SABIC INNOVATIVE NANSHA

Unit Price:
$4556 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility transparent UV resistance High temperature resistan Low viscosity
Application Areas:packing Window encapsulation Industrial applications Aerospace Applications Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24 hr	ASTM D570	0.15	%
	Moisture Absorption	Equilibrium, 23°C	ASTM D570	0.35	%
	Moisture Absorption	Moisture Absorption	Equilibrium, 100°C	ASTM D570	0.58	%
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	18	g/10 min
Specific Volume		ASTM D792	0.830	cm³/g
Outdoor Suitability		UL 746C	f1
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	50.0 mm Span	ASTM D790	2340	Mpa
Flexural Strength	Yield, 50.0 mm Span	ASTM D790	93.0	Mpa
Taber Abrasion Resistance	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg
Tensile Strength	Yield	ASTM D638	62.0	Mpa
Tensile Strength	Tensile Strength	Break	ASTM D638	65.0	Mpa
Tensile Elongation	Yield	ASTM D638	7.0	%
Tensile Elongation	Tensile Elongation	Break	ASTM D638	110	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature		ASTM D15255	154	°C
Specific Heat		ASTM C351	1250	J/kg/°C
Thermal Conductivity		ASTM C177	0.19	W/m/K
RTI		UL 746	100	°C
RTI Imp		UL 746	100	°C
RTI Elec		UL 746	100	°C
Coefficient of Linear Thermal Expansion (Flow)	-40 to 95°C	ASTM E831	6.8E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	132	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		UL 746	PLC 2
Hot-wire Ignition		UL 746	PLC 4
Dielectric Constant	60 Hz	ASTM D150	3.17
	Dielectric Constant	50 kHz	ASTM D150	3.17
	Dielectric Constant	Dielectric Constant	1 MHz	ASTM D150	2.96
Volume Resistivity		ASTM D257	> 1.0E+17	ohms·cm
Dissipation Factor?	50 Hz	ASTM D150	9.0E-4
	Dissipation Factor?	60 Hz	ASTM D150	9.0E-4
	Dissipation Factor?	Dissipation Factor?	1 MHz	ASTM D150	0.010
Dielectric Strength	3.20 mm, in Air	ASTM D149	15	KV/mm
High Amp Arc Ignition		UL 746	PLC 1
High Voltage Arc Tracking Rate		UL 746	PLC 2

Injection	Test Result	Unit
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	280 到 305	°C
Mold Temperature	70 到 95	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	260 到 280	°C
Middle Temperature	270 到 295	°C
Front Temperature	280 到 305	°C
Nozzle Temperature	275 到 300	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Tensile Impact Strength		ASTM D1822	546	kJ/m²
Gardner Impact	23°C	ASTM D3029	169	J
Unnotched Izod Impact Strength	23°C	ASTM D4812	3200	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTM D785	70
Rockwell Hardness	Rockwell Hardness	R-Scale	ASTM D785	118

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index of light		ASTM D542	1.586
Haze	2540 µm	ASTM D1003	1.0	%
Transmittance	2540 µm	ASTM D1003	88.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.76 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.