PC Makrolon® 6717 COVESTRO GERMANY

Unit Price:
$8771 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow	ISO 2577	0.60 到 0.80	%
	Modeling Shrinkage	流量	ISO 2577	0.60 到 0.80	%
		Modeling Shrinkage	Across Flow : 280°C, 2.00 mm 4	ISO 294-4	0.75	%
		Modeling Shrinkage	Modeling Shrinkage	流量 : 2.00 mm 4	ISO 294-4	0.70	%
Moisture Absorption	Saturation, 23°C	ISO 62	0.30	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.12	%
Apparent Density		ISO 60	0.66	g/cm³
Melt Mass-Flow Rate	300°C/1.2 kg	ISO 1133	3.0	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	3.00	cm3/10min
Density	23°C	ISO 1183	1.20	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Strain at Flexural Strength	23°C	ISO 178	7.1	%
Flexural Stress	23°C	ISO 178	98.0	Mpa
Flexural Stress	Flexural Stress	3.5% Strain, 23°C	ISO 178	75.0	Mpa
Nominal Tensile Strain at Break	23°C	ISO 527-2/50	> 50	%
Tensile Stress	Yield, 23°C	ISO 527-2/50	67.0	Mpa
Tensile Stress	Tensile Stress	Break, 23°C	ISO 527-2/50	65.0	Mpa
Tensile Strain	Yield, 23°C	ISO 527-2/50	6.4	%
Tensile Strain	Tensile Strain	Break, 23°C	ISO 527-2/50	110	%
Tensile Modulus	23°C	ISO 527-2/1	2400	Mpa
Flexural Modulus	23°C	ISO 178	2400	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	139	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	127	°C
Vicat Softening Temperature	--	ISO 306/B50	146	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	147	°C
RTI	2.0 mm	UL 746	125	°C
RTI Imp	2.0 mm	UL 746	115	°C
RTI Elec	2.0 mm	UL 746	125	°C
Thermal Conductivity	23°C	ISO 8302	0.20	W/m/K
Linear thermal expansion coefficient	Flow : 23 to 55°C	ISO 11359-2	7.0E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 55°C	ISO 11359-2	7.0E-5	cm/cm/°C
Ball PressureTest	139°C	IEC 60695-10-2	通过
Glass Transition Temperature		ISO 11357-2	146	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	23°C, 1.00 mm	IEC 60243-1	34	KV/mm
Relative Permittivity	23°C, 100 Hz	IEC 60250	3.10
Relative Permittivity	Relative Permittivity	23°C, 1 MHz	IEC 60250	3.00
Comparative Tracking Index	Solution A	IEC 60112	225	V
Comparative Tracking Index	Comparative Tracking Index	Solution B	IEC 60112	125	V
Dissipation Factor?	23°C, 100 Hz	IEC 60250	1.0E-3
Dissipation Factor?	Dissipation Factor?	23°C, 1 MHz	IEC 60250	9.0E-3
Surface Resistivity		IEC 60093	1.0E+16	ohms
Volume Resistivity	23°C	IEC 60093	1.0E+16	ohms·cm

Film	Test Condition	Test Method	Test Result	Unit
Water Vapor Transmission Rate	23°C, 85% RH, 100 µm	ISO 15106-1	15	g/m²/24 hr
Carbon Dioxide Permeability	23°C, 25.4 µm	ISO 2556	16900	cm³/m²/bar/24 hr
Gas Permeation	Carbon Dioxide : 100.0 µm	ISO 2556	3800	cm³/m²/bar/24 hr
	Gas Permeation	Nitrogen : 25.4 µm	ISO 2556	510	cm³/m²/bar/24 hr
		Gas Permeation	Nitrogen : 100.0 µm	ISO 2556	120	cm³/m²/bar/24 hr
			Gas Permeation	Oxygen : 25.4 µm	ISO 2556	2760	cm³/m²/bar/24 hr
			Gas Permeation	Gas Permeation	Oxygen : 100.0 µm	ISO 2556	650	cm³/m²/bar/24 hr

Injection	Test Result	Unit
Suggested Shot Size	30 到 70	%
Rear Temperature	250 到 270	°C
Middle Temperature	270 到 290	°C
Front Temperature	285 到 305	°C
Nozzle Temperature	270 到 305	°C
Back Pressure	10.0 到 20.0	Mpa
Vent Depth	0.025 到 0.075	mm
Drying Temperature ()	120	°C
Dry Air Dryer	4.0	hr
Suggested Max Moisture	< 0.020	%
Processing (Melt) Temp	280 到 320	°C
Mold Temperature	70 到 110	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod Impact Strength	-30°C, Complete Break	ISO 180/A	15	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C, Partial Break	ISO 180/A	60	kJ/m²
Multi-Axial Instrumented Impact Energy	-30°C	ISO 6603-2	65.0	J
Multi-Axial Instrumented Impact Energy	Multi-Axial Instrumented Impact Energy	23°C	ISO 6603-2	60.0	J
Multi-Axial Instrumented Impact Peak Force	-30°C	ISO 6603-2	6400	N
Multi-Axial Instrumented Impact Peak Force	Multi-Axial Instrumented Impact Peak Force	23°C	ISO 6603-2	5500	N
Charpy Unnotched Impact Strength	-60°C	ISO 179/1eU	无断裂
	Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	无断裂
	Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	-30°C, Complete Break	ISO 179/1eA	14	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C, Partial Break	ISO 179/1eA	70	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness		ISO 2039-1	115	Mpa

optical performance	Test Condition	Test Method	Test Result	Unit
Transmittance	1000 µm	ISO 13468-2	87.0	%
	Transmittance	2000 µm	ISO 13468-2	86.0	%
		Transmittance	3000 µm	ISO 13468-2	85.0	%
		Transmittance	Transmittance	4000 µm	ISO 13468-2	84.0	%
ISO Shortname			ISO 7391-PC,MFLR,(,,)-05-9
Index of Refraction		ISO 489	1.586

Flammability	Test Condition	Test Method	Test Result	Unit
Smoke Density	with flame, CO 17	AITM 3.0005	200	ppm
	Smoke Density	with flame, Ds 4 min	ASTM E662	< 200
		Smoke Density	with flame, HCL 17	AITM 3.0005	< 1.0	ppm
			Smoke Density	with flame, HCN 17	AITM 3.0005	notdetectable	ppm
				Smoke Density	with flame, HF 17	AITM 3.0005	< 5.0	ppm
					Smoke Density	with flame, NO-NO2 17	AITM 3.0005	< 5.0	ppm
					Smoke Density	Smoke Density	with flame, SO2-H2O 17	AITM 3.0005	< 20	ppm
Glow Wire Flammability Index	0.75 mm	IEC 60695-2-12	960	°C
	Glow Wire Flammability Index	1.5 mm	IEC 60695-2-12	960	°C
	Glow Wire Flammability Index	Glow Wire Flammability Index	3.0 mm	IEC 60695-2-12	960	°C
Glow Wire Ignition Temperature	0.75 mm	IEC 60695-2-13	875	°C
	Glow Wire Ignition Temperature	1.5 mm	IEC 60695-2-13	900	°C
	Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0 mm	IEC 60695-2-13	900	°C
Burning Rate	> 1.00 mm	ISO 3795	passed
Flame Rating	2.0 mm	UL 94	V-0
Oxygen Index		ISO 4589-2	43	%
Flash Ignition Temperature		ASTM D1929	450	°C
Needle Flame Test	1.50 mm 12	IEC 60695-11-5	2.0	min
	Needle Flame Test	1.50 mm 13	IEC 60695-11-5	2.0	min
		Needle Flame Test	2.00 mm 12	IEC 60695-11-5	2.0	min
			Needle Flame Test	2.00 mm 13	IEC 60695-11-5	2.0	min
				Needle Flame Test	3.00 mm 13	IEC 60695-11-5	2.0	min
				Needle Flame Test	Needle Flame Test	3.00 mm 12	IEC 60695-11-5	2.0	min
Self Ignition Temperature		ASTM D1929	510	°C
Vertical Bunsen Burner Test	1.00 mm 14	FAR 25.853(b)	passed
	Vertical Bunsen Burner Test	1.00 mm 15	FAR 25.853(a)	passed
		Vertical Bunsen Burner Test	3.00 mm 14	FAR 25.853(b)	passed
		Vertical Bunsen Burner Test	Vertical Bunsen Burner Test	3.00 mm 15	FAR 25.853(a)	passed
Application of Flame from Small Burner 11		DIN 53438-1, -3	K1, F1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.