Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Transmittance | 厚度3mm | ASTM D-1003 | 半透明 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | 艾氏、带Notched厚度6.4mm | ASTM D-256 | 50(5) | J/m(kgf·cm/cm) |
Notched Izod Impact Strength | 艾氏、带Notched厚度3.2mm | ASTM D-256 | 50(5) | J/m(kgf·cm/cm) |
Modeling Shrinkage | Flow | ASTM D-955 | 0.3~0.5 | % |
Modeling Shrinkage | Across Flow | ASTM D-955 | 0.3~0.5 | % |
Tensile Strength | Break点 | ASTM D-638 | 56(570) | MPa(Kgf/cm |
Tensile Elongation | Break | ASTM D-638 | >3 | |
Rockwell Hardness | | ASTM D-785 | 93 | M标度 |
Flexural Modulus | | ASTM D-790 | 3920(40000) | MPa(Kgf/cm |
Flexural Strength | | ASTM D-790 | 98(1000) | MPa(Kgf/cm |
Compressive Strength | | ASTM D-695 | 77(790) | MPa(Kgf/cm |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Coefficient of Linear Thermal Expansion | Flow | ASTM D-696 | 5.0 | |
Coefficient of Linear Thermal Expansion | Across Flow | ASTM D-696 | 5.6 | |
Temperature Index | 电学式,厚度1.47mm | UL 746B | 130 | °C |
Temperature Index | 冲击式,厚度1.47mm | UL 746B | 125 | °C |
Temperature Index | 非冲击式,厚度1.47mm | UL 746B | 130 | °C |
Heat Deflection Temperature | 负荷1.813MPa(18.6kgf/cm) | ASTM D-648 | 135 | °C |
Heat Deflection Temperature | 负荷0.451MPa(4.6kgf/cm) | ASTM D-648 | 139 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor (Tangent) | 10 | ASTM D-150 | 0.009 | |
Dissipation Factor (Tangent) | 60Hz | ASTM D-150 | 0.0008 | |
Comparative Tracking Index | | IEC 112 | 180 | V |
Dielectric Constant | 60Hz | ASTM D-150 | 3.51 | |
Dielectric Constant | 10 | ASTM D-150 | 3.41 | |
Arc Resistance | | ASTM D-495 | 100 | sec |
Volume Resistivity | | ASTM D-257 | 1 | |
Insulation failure strength | 快速加压值厚度1.6mm | ASTM D-149 | 30 | KV/mm |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 24hr,23℃ | ASTM D-570 | 0.12 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.