PC PANLITE® ML-1103 TEIJIN JAPAN
137
- Unit Price:
- $4265 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 108.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent High rigidity Thermal stability
- Application Areas:High rigidity Thermal stability transparent
- Color:--
- Grade:Optical grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | ASTM D955 | 0.50-0.70 | % | |
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.20 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.50to0.70 | % |
| MD:4.00mm | 内部方法 | 0.50to0.70 | % | |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.20 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Yield | ISO527-2/50 | 61.0 | Mpa |
| Break | ISO527-2/50 | 59.0 | Mpa | |
| Tensile Strain | Yield | ISO527-2/50 | 6.0 | % |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 50 | % | |
| Tensile Modulus | ASTM D638/ISO 527 | 2400 | kg/cm²(MPa)[Lb/in²] | |
| ISO527-2/1 | 2400 | Mpa | ||
| Tensile Strength | ASTM D638/ISO 527 | 66.0 | kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation | ASTM D638/ISO 527 | 6.0 | % | |
| Flexural Modulus | ASTM D790/ISO 178 | 2300 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Strength | ASTM D790/ISO 178 | 96.0 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Modulus | ISO178 | 2230 | Mpa | |
| Flexural Stress | ISO178 | 93.0 | Mpa | |
| Nominal Tensile Strain at Break | ISO527-2/50 | >50 | % | |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 120 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | ASTM D648/ISO 75 | 141 | ℃（℉） | |
| 0.45MPa,Unannealed | ISO75-2/B | 141 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 129 | °C | |
| Vicat Softening Temperature | ASTM D1525/ISO R306 | 148 | ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.000070 | mm/mm.℃ | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| TD | ISO11359-2 | 7E-05 | cm/cm/°C | |
| Vicat Softening Temperature | ISO306/B50 | 148 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 1.0E+15 | Ω | |
| IEC60093 | >1.0E+15 | ohms | ||
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| ASTM D257/IEC 60093 | 1.0E+15 | Ω.cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | NoBreak |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Transmittance | 3000µm | ASTMD1003 | 47.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.