PC LEXAN™ EXL9300 SABIC INNOVATIVE US
98
- Unit Price:
- $5207 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 85MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Ductility at low temperat Short molding cycle
- Application Areas:Electronic and Electrical Aerospace Applications lens
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.40to0.80 | % |
| TD：3.20mm | 内部方法 | 0.40to0.80 | % | |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.12 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.050 | % | |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 8.0 | g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 7.00 | cm3/10min |
| Outdoor Suitability | UL746C | f1 | ||
| UL746C | f1 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Strength | ISO178 | 86.0 | Mpa | |
| ISO178 | 86.0 | Mpa | ||
| Tensile Elongation | Break | ASTMD638 | 100 | % |
| Flexural Modulus | ISO178 | 2150 | Mpa | |
| ISO178 | 2150 | Mpa | ||
| Tensile Elongation | Yield | ASTMD638 | 6.0 | % |
| Tensile Modulus | ASTMD638 | 2150 | Mpa | |
| ASTMD638 | 2150 | Mpa | ||
| Tensile Strength | Yield | ASTMD638 | 59.0 | Mpa |
| Break | ASTMD638 | 58.0 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 2150 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 86.0 | Mpa |
| Tensile Stress | Yield | ISO527-2/50 | 59.0 | Mpa |
| Break | ISO527-2/50 | 58.0 | Mpa | |
| Tensile Strain | Yield | ISO527-2/50 | 6.0 | % |
| Break | ISO527-2/50 | 100 | % | |
| Tensile Modulus | ISO527-2/1 | 2150 | Mpa | |
| ISO527-2/1 | 2150 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 139 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 126 | °C | |
| Vicat Softening Temperature | ASTMD152511 | 147 | °C | |
| ASTMD152511 | 147 | °C | ||
| -- | ISO306/B50 | 145 | °C | |
| -- | ISO306/B120 | 147 | °C | |
| RTIElec | UL746 | 125 | °C | |
| UL746 | 125 | °C | ||
| Evolution Calendar intelligent importer | UL746 | 110 | °C | |
| UL746 | 110 | °C | ||
| RTIStr | UL746 | 125 | °C | |
| UL746 | 125 | °C | ||
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass | |
| Heat Deflection Temperature | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 139 | °C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 126 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot-wire Ignition | HWI | UL746 | PLC2 | |
| High Amp Arc Ignition | HAI | UL746 | PLC0 | |
| Comparative Tracking Index | CTI | UL746 | PLC2 | |
| Comparative Tracking Index | IEC60112 | 250 | V | |
| IEC60112 | 250 | V |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 50 | kJ/m² |
| 23°C | ISO179/1eA | 70 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Notched Izod Impact Strength | 23°C | ISO180/1A | 75 | kJ/m² |
| -30°C | ISO180/1A | 50 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 900 | °C |
| UL flame retardant rating | 0.8mm | UL94 | V-0 | |
| 2.0mm | UL94 | 5VB | ||
| 2.5mm | UL94 | 5VA | ||
| GlowWireFlammability | 1.9mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.