Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ASTMD955 | 0.50到0.70 | % |
Modeling Shrinkage | MD | ISO294-4 | 0.50到0.70 | % |
Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238,ISO1133 | 10 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | Yield,3.20mm,Injection3 | ASTMD638 | 60.0 | Mpa |
Tensile Strength | Yield,4.00mm,Injection | ISO527-2/50 | 60.0 | Mpa |
Tensile Strength | Break,3.20mm,Injection | ASTMD638 | 57.9 | Mpa |
Tensile Strength | Break,4.00mm,Injection | ISO527-2/50 | 58.0 | Mpa |
Tensile Modulus | 3.20mm,Injection | ASTMD638 | 2210 | Mpa |
Tensile Modulus | 4.00mm,Injection | ISO527-2/50 | 2200 | Mpa |
Tensile Elongation | Yield,3.20mm,Injection | ASTMD638 | 6.2 | % |
Tensile Elongation | Yield,4.00mm,Injection | ISO527-2/50 | 6.0 | % |
Tensile Elongation | Break,3.20mm,Injection | ASTMD638 | 110 | % |
Tensile Elongation | Break,4.00mm,Injection | ISO527-2/50 | 110 | % |
Flexural Modulus | 3.20mm,Injection | ASTMD790 | 2400 | Mpa |
Flexural Modulus | 4.00mm,Injection4 | ISO178 | 2400 | Mpa |
Flexural Strength | 3.20mm,Injection | ASTMD790 | 93.8 | Mpa |
Flexural Strength | 4.00mm,Injection4 | ISO178 | 94.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648,ISO75-2/B | 139 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 127 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 125 | °C |
Vicat Softening Temperature | -- | ASTMD15256 | 149 | °C |
Vicat Softening Temperature | -- | ISO306/A120 | 150 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 144 | °C |
RTIElec | | UL746 | 125 | °C |
Evolution Calendar intelligent importer | | UL746 | 125 | °C |
Linear thermal expansion coefficient | MD:-22to85°C | ASTMD696 | 6.5E-05 | cm/cm/°C |
RTI | | UL746 | 125 | °C |
Ball Indentation Temperature | | IEC60335-1 | >125 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Instrumented Dart Impact | 23°C,3.20mm,总能量 | ASTMD3763 | 58.8 | J |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale,3.20mm,Injection | ASTMD785 | 123 | |
Rockwell Hardness | R-Sale,4.00mm | ISO2039-2 | 123 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.6mm | UL94 | V-0 | |
Glow Wire Ignition Temperature | 2.0mm | IEC60695-2-13 | 960 | °C |
Oxygen Index | | ASTMD2863,ISO4589-2 | 35 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.