Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.20mm | ASTMD955 | 0.10to0.30 | % |
Melt Mass-Flow Rate | 250°C/10.0kg | ASTMD1238 | 7.0 | g/10min |
Melt Mass-Flow Rate | 250°C/10.0kg | ISO1133 | 5.4 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Modulus | | ASTMD790 | 7700 | Mpa |
Tensile Strength | Yield | ASTMD638 | 130 | Mpa |
Flexural Strength | | ASTMD790 | 200 | Mpa |
Flexural Stress | | ISO178 | 153 | Mpa |
Tensile Stress | Yield | ISO527-2/50 | 115 | Mpa |
Tensile Stress | Break | ISO527-2/50 | 115 | Mpa |
Tensile Strain | Break | ISO527-2/50 | 2.7 | % |
Tensile Modulus | | ISO527-2/50 | 7200 | Mpa |
Flexural Modulus | | ISO178 | 7900 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | -- | ISO306/B50 | 150 | °C |
Vicat Softening Temperature | -- | ISO306/B120 | 151152 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 146 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 143 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 142 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Constant | 1MHz | ASTMD150 | 3.30 | |
Dissipation Factor? | 1MHz | ASTMD150 | 9E-03 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
CharpyNotchedImpactStrength5 | 23°C | ISO179/1eA | 11 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ASTMD785 | 93 | |
Rockwell Hardness | R-Scale | ISO2039-2 | 119 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | V-2V-1 | |
UL flame retardant rating | 3.0mm | UL94 | V-0 | |
UL flame retardant rating | 6.0mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.