PC IUPILON™ EFR3000 MITSUBISHI ENGINEERING JAPAN
73
- Unit Price:
- $3896 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Flame retardant
- Application Areas:Non specific food
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | ASTM D955 | 0.50-0.70 | % | |
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.24 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD:3.20mm | 0.50to0.70 | % | |
| MD:3.20mm | 0.50to0.70 | % | ||
| 吸水率(Saturation,23°C) | 0.24 | % | ||
| Melt Mass-Flow Rate | 300°C/1.2kg | ISO1133 | 22 | g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 21.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal Tensile Strain at Break | ISO527-2 | 67 | % | |
| Flexural Stress | ISO178 | 92.0 | Mpa | |
| Tensile Stress | Yield | ISO527-2 | 61.0 | Mpa |
| Tensile Strain | Yield | ISO527-2 | 4.7 | % |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 4.7 | % | |
| Tensile Modulus | ASTM D638/ISO 527 | 2300 | kg/cm²(MPa)[Lb/in²] | |
| ISO527-2 | 2300 | Mpa | ||
| Tensile Strength | ASTM D638/ISO 527 | 61.0 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Modulus | ASTM D790/ISO 178 | 2500 | kg/cm²(MPa)[Lb/in²] | |
| ISO178 | 2500 | Mpa | ||
| Flexural Strength | ASTM D790/ISO 178 | 92.0 | kg/cm²(MPa)[Lb/in²] |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | ASTM D648/ISO 75 | 137 | ℃（℉） | |
| 0.45MPa,Unannealed | ISO75-2/B | 137 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 125 | °C | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.000067 | mm/mm.℃ | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 6.6E-05 | cm/cm/°C |
| TD | ISO11359-2 | 6.7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation Factor? | 100Hz | IEC60250 | 6E-04 | |
| 1MHz | IEC60250 | 9E-03 | ||
| Dielectric Strength | 1.00mm | IEC60243-1 | 31 | KV/mm |
| 3.00mm | IEC60243-1 | 18 | KV/mm | |
| Relative Permittivity | 100Hz | IEC60250 | 3.10 | |
| 1MHz | IEC60250 | 3.10 | ||
| Surface Resistivity | ASTM D257/IEC 60093 | 6.0E+15 | Ω | |
| IEC60093 | 6E+15 | ohms | ||
| Dielectric Constant | ASTM D150/IEC 60250 | 3.10 | ||
| Volume Resistivity | ASTM D257/IEC 60093 | 3.0E+16 | Ω.cm | |
| IEC60093 | 3E+16 | ohms·cm | ||
| Dielectric loss | ASTM D150/IEC 60250 | 0.00060 | ||
| ASTM D150/IEC 60250 | 0.0090 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | NoBreak |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 1.0mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.