PC LEXAN™ BFL4000U WH3150 SABIC INNOVATIVE NANSHA
63
- Unit Price:
- $3237 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 51MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance Flame retardant
- Application Areas:Lighting applications
- Color:--
- Grade:Light diffusion level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.35 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 24 | g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 22.0 | cm3/10min |
| Density / Specific Gravity | ASTMD792 | 1.38 | g/cm³ | |
| ISO1183 | 1.38 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | Yield | ASTMD638 | 5.0 | % |
| Tensile Modulus | ASTMD638 | 2240 | Mpa | |
| Tensile Strength | Yield | ASTMD638 | 54.0 | Mpa |
| Break | ASTMD638 | 47.0 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 2050 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 90.0 | Mpa |
| Tensile Elongation | Break | ASTMD638 | 56 | % |
| Flexural Modulus | ISO178 | 2170 | Mpa | |
| Flexural Strength | ISO178 | 83.0 | Mpa | |
| Tensile Stress | Yield | ISO527-2/5 | 50.0 | Mpa |
| Break | ISO527-2/5 | 44.0 | Mpa | |
| Tensile Strain | Break | ISO527-2/5 | 74 | % |
| Yield | ISO527-2/5 | 6.0 | % | |
| Tensile Modulus | ISO527-2/1 | 2040 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 124 | °C |
| 1.8MPa,Annealed,3.20mm | ASTMD648 | 115 | °C | |
| 0.45MPa,Unannealed,3.20mm | ASTMD648 | 131 | °C | |
| 0.45MPa,Unannealed,6.40mm | ASTMD648 | 134 | °C | |
| Vicat Softening Temperature | ASTMD152510 | 136 | °C | |
| -- | ISO306/B50 | 137 | °C | |
| -- | ISO306/B120 | 139 | °C | |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 7.5E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 7.5E-05 | cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 115 | °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 130 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 30 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 20 | kJ/m² |
| 23°C | ISO180/1A | 30 | kJ/m² | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 68.0 | J |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 240 | J/m |
| 23°C | ASTMD256 | 470 | J/m |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.