PC LEXAN™ FXD1414T BL4E059X SABIC INNOVATIVE SHANGHAI
75
- Unit Price:
- $5196 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low temperature resistanc transparent Easy to process Middle flow
- Application Areas:Electrical field Electronic field Household appliances Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow 2 | 内部方法 | 0.40 到 0.80 | % |
| Flow : 3.20 mm | 内部方法 | 0.40 到 0.80 | % | |
| Across Flow : 3.20 mm | 内部方法 | 0.40 到 0.80 | % | |
| Moisture Absorption | Saturation, 23°C | ISO 62 | 0.12 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.090 | % | |
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 10 | g/10 min |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 9.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | -- 3 | ASTM D638 | 2240 | Mpa |
| -- | ISO 527-2/1 | 2300 | Mpa | |
| Tensile Elongation | Yield 4 | ASTM D638 | 5.8 | % |
| Yield | ISO 527-2/50 | 5.4 | % | |
| Break 4 | ASTM D638 | 84 | % | |
| Break | ISO 527-2/50 | 110 | % | |
| Flexural Modulus | 50.0 mm Span 5 | ASTM D790 | 2220 | Mpa |
| -- 6 | ISO 178 | 2150 | Mpa | |
| Tensile Strength | Yield 4 | ASTM D638 | 59.0 | Mpa |
| Yield | ISO 527-2/50 | 57.0 | Mpa | |
| Break 4 | ASTM D638 | 51.0 | Mpa | |
| Break | ISO 527-2/50 | 54.0 | Mpa | |
| Flexural Stress | -- 6, 7 | ISO 178 | 89.0 | Mpa |
| Yield, 50.0 mm Span 5 | ASTM D790 | 85.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | -- | ASTM D152511, ISO 306/B5011 | 138 | °C |
| -- | ISO 306/B120 | 142 | °C | |
| Linear thermal expansion coefficient | Flow : -40 to 95°C | ASTM E831 | 6.7E-5 | cm/cm/°C |
| Flow : 23 to 80°C | ISO 11359-2 | 6.7E-5 | cm/cm/°C | |
| Across Flow : -40 to 95°C | ASTM E831 | 8.0E-5 | cm/cm/°C | |
| Across Flow : 23 to 80°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C | |
| Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 122 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 10 | ISO 75-2/Af | 116 | °C | |
| Ball PressureTest | 123 to 127°C | IEC 60695-10-2 | 通过 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Time | 3.0 到 4.0 | hr | ||
| Suggested Shot Size | 40 到 60 | % | ||
| Rear Temperature | 215 到 295 | °C | ||
| Middle Temperature | 280 到 305 | °C | ||
| Front Temperature | 295 到 315 | °C | ||
| Nozzle Temperature | 290 到 310 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 40 到 70 | rpm | ||
| Vent Depth | 0.025 到 0.076 | mm | ||
| Drying Temperature | 120 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 295 到 315 | °C | ||
| Mold Temperature | 70 到 95 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 | ||
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 60 | kJ/m² |
| 23°C | ISO 179/1eA | 70 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 76.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.