PC LEXAN™ 4701R-110001 SABIC INNOVATIVE US

Unit Price:
$4913 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
18.8MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan transparent
Application Areas:Electronic and electrical
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24 hr	ASTM D570	0.19	%
Specific Volume		ASTM D792	0.830	cm³/g
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	2.0	g/10 min
Melt Mass-Flow Rate	Melt Mass-Flow Rate	300°C/6.1 kg	ASTM D1238	9.0	g/10 min
Melt Volume flow Rate	300°C/5.0 kg	ISO 1133	6.00	cm3/10min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.80 到 1.0	%
Modeling Shrinkage - Flow		内部方法	0.90	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength	Yield	ASTM D638	65.0	Mpa
Tensile Strength	Tensile Strength	Break	ASTM D638	77.0	Mpa
Flexural Modulus		ISO 178	2300	Mpa
Tensile Stress	Yield	ISO 527-2/50	70.0	Mpa
Tensile Strain	Yield	ISO 527-2/50	7.0	%
Tensile Strain	Tensile Strain	Break	ISO 527-2/50	> 50	%
Tensile Modulus		ISO 527-2/1	2300	Mpa
Tensile Elongation	Break	ASTM D638	78	%
Flexural Modulus	50.0 mm Span	ASTM D790	2330	Mpa
Flexural Strength	Yield, 50.0 mm Span	ASTM D790	97.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
RTI		UL 746	130	°C
RTI Imp		UL 746	130	°C
RTI Elec		UL 746	130	°C
Coefficient of Linear Thermal Expansion (Flow)	23 to 80°C	ISO 11359-2	8.0E-5	cm/cm/°C
Coefficient of Linear Thermal Expansion (Flow)	Coefficient of Linear Thermal Expansion (Flow)	-40 to 95°C	ASTM E831	8.1E-5	cm/cm/°C
Specific Heat		ASTM C351	1260	J/kg/°C
Thermal Conductivity		ASTM C177	0.21	W/m/K
Thermal Conductivity	Thermal Conductivity		ISO 8302	0.21	W/m/K
Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	148	°C
Ball PressureTest	123 to 127°C	IEC 60695-10-2	通过
Heat Deflection Temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	165	°C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	150	°C
Vicat Softening Temperature	--	ISO 306/A50	185	°C
	Vicat Softening Temperature	--	ISO 306/B50	175	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	170	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
High Amp Arc Ignition		UL 746	PLC 3
Arc Resistance		ASTM D495	PLC 6
Comparative Tracking Index		UL 746	PLC 3
Hot-wire Ignition		UL 746	PLC 2
High Voltage Arc Tracking Rate		UL 746	PLC 3
Dielectric Constant	60 Hz	ASTM D150	3.27
	Dielectric Constant	50 kHz	ASTM D150	3.27
	Dielectric Constant	Dielectric Constant	1 MHz	ASTM D150	3.10
Volume Resistivity		ASTM D257	> 2.5E+17	ohms·cm
Dissipation Factor?	100 Hz	IEC 60250	0.026
	Dissipation Factor?	50 Hz	ASTM D150	1.6E-3
		Dissipation Factor?	60 Hz	ASTM D150	1.6E-3
		Dissipation Factor?	Dissipation Factor?	100 Hz	ASTM D150	0.026
Dielectric Strength	3.20 mm, in Air	ASTM D149	20	KV/mm
Relative Permittivity	1 MHz	IEC 60250	3.10

Injection	Test Condition	Test Result	Unit
Drying Temperature		125 到 135	°C
Drying Temperature	Drying Temperature		120	°C
Suggested Max Moisture		0.020	%
Processing (Melt) Temp		325 到 360	°C
Processing (Melt) Temp	Processing (Melt) Temp		350 到 370	°C
Mold Temperature		80 到 115	°C
Mold Temperature	Mold Temperature		100 到 125	°C
Hopper Temperature		60 到 80	°C
Drying Time		3.0 到 4.0	hr
Suggested Shot Size		40 到 60	%
Rear Temperature		325 到 350	°C
Rear Temperature	Rear Temperature		300 到 320	°C
Middle Temperature		310 到 330	°C
Middle Temperature	Middle Temperature		340 到 360	°C
Front Temperature		350 到 370	°C
Front Temperature	Front Temperature		320 到 340	°C
Nozzle Temperature		320 到 340	°C
Nozzle Temperature	Nozzle Temperature		345 到 365	°C
Back Pressure		0.300 到 0.700	Mpa
Screw Speed		40 到 70	rpm
Vent Depth		0.025 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Gardner Impact	23°C	ASTM D3029	149	J
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	13	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	46	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	无断裂
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	无断裂
Notched Izod Impact Strength	-30°C	ISO 180/1A	11	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO 180/1A	35	kJ/m²
Unnotched Izod Impact Strength	-30°C	ISO 180/1U	无断裂
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C	ISO 180/1U	无断裂
Unnotched Izod Impact Strength	23°C	ASTM D4812	3200	J/m
Tensile Impact Strength		ASTM D1822	577	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R -Sale	ISO 2039-2	127
	Rockwell Hardness	M-Scale	ASTM D785	92
	Rockwell Hardness	Rockwell Hardness	R-Scale	ASTM D785	127

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index of light		ASTM D542	1.600
Haze	2540 µm	ASTM D1003	1.0	%
Transmittance	2540 µm	ASTM D1003	85.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Flammability Index	2.0 mm	IEC 60695-2-12	850	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.