Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ASTM D-955 | 0.002-0.004 | mm/mm |
辉光灯丝测试 | | IEC 695-2-1 | 960 | °C |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Unnotched Izod Impact Strength | 23℃ | ASTM D-256 | 380 | J/m |
Tensile Strength(Break) | | ASTM D-638 | 80 | Mpa |
IZOD Notch Impact Strength | 23℃ | ASTM D-256 | 75 | J/m |
Tensile Modulus | | ASTM D-638 | 6000 | Mpa |
Tensile Elongation | Break | ASTM D-638 | 4 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.82MPa,Unannealed | ASTM D-648 | 135 | °C |
Deflection Temperature Under Load? | 1.82MPa,Annealed | ASTM D-648 | 146 | °C |
Vicat Softening Temperature | 50N,50℃/hr | ASTM D-1525 | 145 | °C |
Ball PressureTest | | IEC 598-1 | >125 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Comparative Tracking Index | 2.0mm | IEC 112 | 175 | V |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Melt index | 300℃,1.2kg | ASTM D-1238 | 15 | g/10min |
Density | | ASTM D-792 | 1370 | kg/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.