PC LEXAN™ HF1110R-111 SABIC INNOVATIVE SINGAPHORE

Unit Price:
$2814 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility Good demolding performanc Good forming performance
Application Areas:Safety equipment Thin walled products Optical data storage lens container
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	25	g/10 min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	Break	ASTM D638	120	%
Flexural Modulus	50.0 mm Span	ASTM D790	2300	Mpa
Flexural Strength	Yield, 50.0 mm Span	ASTM D790	93.0	Mpa
Tensile Strength	Yield	ASTM D638	62.0	Mpa
Tensile Strength	Tensile Strength	Break	ASTM D638	65.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	126	°C
RTI		UL 746	130	°C
RTI Imp		UL 746	130	°C
RTI Elec		UL 746	130	°C

Electrical performance	Test Method	Test Result
High Voltage Arc Tracking Rate	UL 746	PLC 2
Comparative Tracking Index	UL 746	PLC 2
Hot-wire Ignition	UL 746	PLC 2
High Amp Arc Ignition	UL 746	PLC 1

Injection	Test Result	Unit
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	270 到 295	°C
Mold Temperature	70 到 95	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	250 到 270	°C
Middle Temperature	260 到 280	°C
Front Temperature	270 到 295	°C
Nozzle Temperature	265 到 290	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Tensile Impact Strength		ASTM D1822	378	kJ/m²
Instrumented Dart Impact	23°C, Energy at Peak	ASTM D3763	54.0	J

optical performance	Test Condition	Test Method	Test Result	Unit
Transmittance	2540 µm	ASTM D1003	88.0	%
Haze	2540 µm	ASTM D1003	1.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.1 mm	UL 94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.