PC PANLITE® GN-3620L TEIJIN JAPAN
71
- Unit Price:
- $3741 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 46MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity Glass fiber reinforced
- Application Areas:Electrical components Industrial applications
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | ASTM D955 | 0.40-0.60 | % | |
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.14 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.40to0.60 | % |
| MD:4.00mm | 内部方法 | 0.10to0.30 | % | |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.14 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Break | ISO527-2/5 | 82.0 | Mpa |
| Tensile Strain | Break | ISO527-2/5 | 1.0 | % |
| Flexural Modulus | ISO178 | 5600 | Mpa | |
| Flexural Stress | ISO178 | 138 | Mpa | |
| Tensile Modulus | ASTM D638/ISO 527 | 6100 | kg/cm²(MPa)[Lb/in²] | |
| ISO527-2/1 | 6100 | Mpa | ||
| Tensile Strength | ASTM D638/ISO 527 | 82.0 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Modulus | ASTM D790/ISO 178 | 5600 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Strength | ASTM D790/ISO 178 | 138 | kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 1.0 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | ASTM D648/ISO 75 | 145 | ℃（℉） | |
| 0.45MPa,Unannealed | ISO75-2/B | 145 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 140 | °C | |
| Vicat Softening Temperature | ASTM D1525/ISO R306 | 147 | ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.000030 | mm/mm.℃ | |
| RTIElec | 1.5mm | UL746 | 80.0 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 80.0 | °C |
| RTIStr | 1.5mm | UL746 | 80.0 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 3E-05 | cm/cm/°C |
| TD | ISO11359-2 | 6E-05 | cm/cm/°C | |
| Vicat Softening Temperature | ISO306/B50 | 147 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation Factor? | 100Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 9E-03 | ||
| Comparative Tracking Index | IEC60112 | 175 | V | |
| Dielectric Strength | IEC60243-1 | 35 | KV/mm | |
| Surface Resistivity | ASTM D257/IEC 60093 | 1.0E+15 | Ω | |
| IEC60093 | >1.0E+15 | ohms | ||
| Dielectric Constant | 100Hz | IEC60250 | 3.40 | |
| 1MHz | IEC60250 | 3.40 | ||
| ASTM D150/IEC 60250 | 3.40 | |||
| Volume Resistivity | ASTM D257/IEC 60093 | 1.0E+15 | Ω.cm | |
| IEC60093 | >1.0E+15 | ohms·cm | ||
| Dielectric loss | ASTM D150/IEC 60250 | 0.0010 | ||
| ASTM D150/IEC 60250 | 0.0090 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO179 | 40 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL94 | V-2 | |
| 1.0mm4 | UL94 | V-1 | ||
| 1.6mm | UL94 | V-0 | ||
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 | °C |
| 1.6mm | IEC60695-2-12 | 960 | °C | |
| 3.0mm | IEC60695-2-12 | 960 | °C | |
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 825 | °C |
| 1.6mm | IEC60695-2-13 | 850 | °C | |
| 3.0mm | IEC60695-2-13 | 850 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.