Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Spiral Flow | 3mm厚 | 出光法 | 0.13 | CM |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation | | ISO R-527 (ASTM D-638) | 5700(58000) | MPa(KG/cm |
| Tensile Elongation?(Break) | | ISO R-527 (ASTM D-638) | 4 | % |
| Tensile Strength (Break) | | ISO R-527 (ASTM D-638) | 100(1000) | MPa(KG/cm |
| Tensile Modulus | | ISO 178 (ASTM D-790) | 5880(60000) | MPa(KG/cm |
| Rockwell Hardness | | ISO 2039-2 (ASTM D-785) | M91 | |
| Flexural strength | | ISO 178 (ASTM D-790) | 140(1400) | Mpa |
| Izod Impact Strength | 4mm with notch 3.2mm with notch | ISO 180 (ASTM D-256) | 13(14) | KJ/m |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability | 1.47mm厚 | UL 94 | V-2 | |
| Vicat Softening Temperature | | ISO 306 | 150 | °C |
| Heat Deflection Temperature | 1.80MPa,18.6kg/cm | ISO 75(ASTM D-648) | 139 | °C |
| Coefficient of Linear Thermal Expansion | | ASTM D-696 | 2.5 | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Constant | 60Hz | ASTM D-150 | 8×10 | |
| Dielectric Constant | 10 | ASTM D-150 | 9×10 | |
| Volume Resistivity | | ASTM D-257 | ＜10 | Ω·cm |
| Insulation Resistance | 1.6mm厚 | ASTM D-149 | ＜22 | KV/mm |
| Arc Resistance | | ASTM D-495 | 110 | sec |
| Dissipation Factor | 10 | ASTM D-150 | 3.15 | |
| Dissipation Factor | 60Hz | ASTM D-150 | 3.25 | |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD | ASTM D-955 | 2.0 | |
| Modeling Shrinkage | TD | ASTM D-955 | 6.0 | |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 23℃水中24h | ASTM D-570 | 0.13 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.