PC IUPILON™ GS2010MR2 MITSUBISHI ENGINEERING JAPAN

Unit Price:
$3485 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
25MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant enhance Filler: Glass fiber reinf 10% filler by weight
Application Areas:fibre
Color:--
Grade:Enhanced level

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ASTM D792/ISO 1183	1.27
Modeling Shrinkage		ASTM D955	0.3 - 0.5	%

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD:3.20mm		0.40to0.60	%
Modeling Shrinkage	Modeling Shrinkage	MD:3.20mm		0.30to0.50	%
Moisture Absorption	Saturation,23°C	ISO62	0.14	%
Melt Mass-Flow Rate	300°C/1.2kg	ISO1133	10	g/10min
Melt Volume flow Rate	300°C/1.2kg	ISO1133	9.00	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress		ISO178	135	Mpa
Tensile Stress	Break	ISO527-2	78.0	Mpa
Tensile Strain	Break	ISO527-2	2.9	%
Tensile Elongation?(Break)		ASTM D638/ISO 527	3.8	%
Tensile Modulus		ASTM D638/ISO 527	4400	kg/cm²(MPa)[Lb/in²]
Tensile Modulus	Tensile Modulus		ISO527-2	4500	Mpa
Flexural Modulus		ASTM D790/ISO 178	3900	kg/cm²(MPa)[Lb/in²]
Flexural Modulus	Flexural Modulus		ISO178	4000	Mpa
Flexural Strength		ASTM D790/ISO 178	130	kg/cm²(MPa)[Lb/in²]

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	145	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	140	°C
Linear expansion coefficient		ASTM D696/ISO 11359	4.0E-05	mm/mm.℃
Linear thermal expansion coefficient	MD	ISO11359-2	4E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	6.7E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index	CTI	UL746	PLC4

Processing	Test Condition	Test Method	Test Result	Unit
Mold Temperature			80-120	°C
Processing temperature			270-290	°C
	Processing temperature			290-310	°C
	Processing temperature	Processing temperature			280-300	°C
Drying conditions			热风干燥 120℃---約4-8小时
Screw Speed			50-100	rpm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	23°C	ISO179	55	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.75mm	UL94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.