Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Flow : 24hr | ASTM D955 | 0.70 到 0.90 | % |
Modeling Shrinkage | Across Flow : 24hr | ASTM D955 | 0.70 到 0.90 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation | Break | ASTM D638 | 53 | % |
Flexural Modulus | | ASTM D790 | 2270 | Mpa |
Flexural Strength | | ASTM D790 | 81.0 | Mpa |
Tensile Strength | Break | ASTM D638 | 53.0 | Mpa |
Coefficient of Friction | Dynamic | ASTM D3702 | 0.28 | |
Coefficient of Friction | Static | ASTM D3702 | 0.17 | |
Specific Wear Rate | | ASTM D3702 | 2.0E+7 | 10^-8 mm³/N·m |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 128 | °C |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Time | | | 4.0 | hr |
Rear Temperature | | | 295 到 305 | °C |
Middle Temperature | | | 305 到 315 | °C |
Front Temperature | | | 310 到 320 | °C |
Back Pressure | | | 0.200 到 0.300 | Mpa |
Screw Speed | | | 30 到 60 | rpm |
Drying Temperature | | | 120 | °C |
Suggested Max Moisture | | | 0.020 | % |
Processing (Melt) Temp | | | 300 到 315 | °C |
Mold Temperature | | | 80 到 110 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 无断裂 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.