PC LEXAN™ HF1140-111 SABIC INNOVATIVE NANSHA

Unit Price:
$2945 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
11MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility Good demolding performanc Good forming performance
Application Areas:Safety equipment packing Thin walled products Optical data storage lens container
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24 hr	ASTM D570	0.15	%
	Moisture Absorption	Equilibrium, 23°C	ASTM D570	0.35	%
	Moisture Absorption	Moisture Absorption	Equilibrium, 100°C	ASTM D570	0.58	%
Specific Volume		ASTM D792	0.830	cm³/g
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	25	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	23.0	cm3/10min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Taber Abrasion Resistance	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg
Tensile Strength	Yield 3	ASTM D638	62.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	63.0	Mpa
		Tensile Strength	Break 3	ASTM D638	65.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	50.0	Mpa
Flexural Stress	-- 5, 6	ISO 178	90.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	93.0	Mpa
Tensile Modulus	-- 2	ASTM D638	2370	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2350	Mpa
Tensile Elongation	Yield 3	ASTM D638	6.0	%
	Tensile Elongation	Yield	ISO 527-2/50	6.0	%
		Tensile Elongation	Break 3	ASTM D638	120	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	70	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2300	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2300	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ISO 306/B50	139	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	140	°C
Specific Heat		ASTM C351	1250	J/kg/°C
Thermal Conductivity	--	ASTM C177	0.19	W/m/K
Thermal Conductivity	Thermal Conductivity	--	ISO 8302	0.20	W/m/K
RTI		UL 746	130	°C
RTI Imp		UL 746	130	°C
RTI Elec		UL 746	130	°C
Coefficient of Linear Thermal Expansion (Flow)	-40 to 95°C	ASTM E831	6.8E-5	cm/cm/°C
Coefficient of Linear Thermal Expansion (Flow)	Coefficient of Linear Thermal Expansion (Flow)	23 to 80°C	ISO 11359-2	7.0E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 11	ISO 75-2/Be	133	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	126	°C
			Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	126	°C
			Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 11	ISO 75-2/Ae	121	°C
Ball PressureTest	123 to 127°C	IEC 60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		UL 746	PLC 2
Hot-wire Ignition		UL 746	PLC 2
Dielectric Strength	3.20 mm, in Air	ASTM D149	15	KV/mm
Dielectric Strength	Dielectric Strength	3.20 mm, in Oil	IEC 60243-1	17	KV/mm
Dissipation Factor?	50 Hz	ASTM D150	9.0E-4
	Dissipation Factor?	60 Hz	ASTM D150	9.0E-4
		Dissipation Factor?	1 MHz	ASTM D150, IEC 60250	0.010
			Dissipation Factor?	50 Hz	IEC 60250	1.0E-3
			Dissipation Factor?	Dissipation Factor?	60 Hz	IEC 60250	1.0E-3
Surface Resistivity		IEC 60093	> 1.0E+15	ohms
Dielectric Constant	60 Hz	ASTM D150	3.17
	Dielectric Constant	50 kHz	ASTM D150	3.17
		Dielectric Constant	1 MHz	ASTM D150	2.96
			Dielectric Constant	50 Hz	IEC 60250	2.70
				Dielectric Constant	60 Hz	IEC 60250	2.70
				Dielectric Constant	Dielectric Constant	1 MHz	IEC 60250	2.70
Volume Resistivity	--	ASTM D257	> 1.0E+17	ohms·cm
Volume Resistivity	Volume Resistivity	--	IEC 60093	> 1.0E+15	ohms·cm
High Voltage Arc Tracking Rate		UL 746	PLC 2
High Amp Arc Ignition		UL 746	PLC 1

Injection	Test Result	Unit
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	250 到 270	°C
Middle Temperature	260 到 280	°C
Front Temperature	270 到 295	°C
Nozzle Temperature	265 到 290	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	270 到 295	°C
Mold Temperature	70 到 95	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Tensile Impact Strength		ASTM D1822	378	kJ/m²
Unnotched Izod Impact Strength	23°C	ASTM D4812	3200	J/m
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	12	kJ/m²
Gardner Impact	23°C	ASTM D3029	169	J
Instrumented Dart Impact	23°C, Energy at Peak	ASTM D3763	54.0	J

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTM D785	70
Rockwell Hardness	Rockwell Hardness	R-Scale	ASTM D785	118

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index of light		ASTM D542	1.586
Haze	2540 µm	ASTM D1003	1.0	%
Transmittance	2540 µm	ASTM D1003	88.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
Oxygen Index		ISO 4589-2	25	%
Flame Rating	1.1 mm	UL 94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.