PC INFINO® HF-1023IM Samsung Cheil South Korea
91
- Unit Price:
- $3110 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance High mobility Impact resistance High liquidity
- Application Areas:Electrical field Electronic field Phone case
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow : 3.20 mm | ASTM D955 | 0.44 到 0.53 | % |
| Across Flow : 3.20 mm | ASTM D955 | 0.45 到 0.55 | % | |
| Across Flow : 2.00 mm | ISO 294-4 | 0.45 到 0.55 | % | |
| 流量 : 2.00 mm | ISO 294-4 | 0.44 到 0.53 | % | |
| Moisture Absorption | Saturation, 23°C | ASTM D570 | 0.35 | % |
| Melt Mass-Flow Rate | 250°C/10.0 kg | ASTM D1238, ISO 1133 | 22 | g/10 min |
| Density / Specific Gravity | 本色 | ASTM D792, ISO 1183 | 1.18 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | Yield 3 | ASTM D638 | 59.0 | Mpa |
| Yield | ISO 527-2/50 | 60.0 | Mpa | |
| Break 3 | ASTM D638 | 69.0 | Mpa | |
| Break | ISO 527-2/50 | 96.0 | Mpa | |
| Tensile Modulus | -- 3 | ASTM D638 | 1900 | Mpa |
| -- | ISO 527-2/50 | 2100 | Mpa | |
| Tensile Elongation | Break 3 | ASTM D638 | 120 | % |
| Break | ISO 527-2/50 | 100 | % | |
| Flexural Modulus | -- 4 | ASTM D790 | 2000 | Mpa |
| -- 5 | ISO 178 | 2100 | Mpa | |
| Flexural Strength | -- 4 | ASTM D790 | 83.0 | Mpa |
| -- 5 | ISO 178 | 88.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 4.00 mm | ISO 75-2/B | 133 | °C |
| 0.45 MPa, Annealed, 4.00 mm | ISO 75-2/B | 130 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 126 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | ISO 75-2/A | 120 | °C | |
| 1.8 MPa, Annealed, 4.00 mm | ISO 75-2/A | 120 | °C | |
| Vicat Softening Temperature | -- | ISO 306/B50 | 140 | °C |
| -- | ISO 306/B120 | 142 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rear Temperature | 270 | °C | ||
| Middle Temperature | 280 | °C | ||
| Front Temperature | 290 | °C | ||
| Nozzle Temperature | 300 | °C | ||
| Back Pressure | 0.981 到 2.94 | Mpa | ||
| Screw Speed | 40 到 80 | rpm | ||
| Injection Pressure | 98.1 | Mpa | ||
| Desiccant Dryer | 2.0 到 4.0 | hr | ||
| 100 | °C | |||
| vacuum dryer | 100 | °C | ||
| 4.0 到 6.0 | hr | |||
| Suggested Max Moisture | < 0.020 | % | ||
| Mold Temperature | 80 到 100 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 68 | kJ/m² |
| Notched Izod Impact Strength | 23°C, 3.18 mm | ASTM D256 | 690 | J/m |
| 23°C, 6.35 mm | ASTM D256 | 540 | J/m | |
| 23°C 6 | ISO 180/1A | 63 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ASTM D785 | 120 | |
| R -Sale | ISO 2039-2 | 120 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.