PC LEXAN™ 505R SABIC INNOVATIVE US
76
- Unit Price:
- $3263 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 31MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Middle flow Thermal stability
- Application Areas:Electronic display Lighting applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：--2 | 内部方法 | 0.20to0.60 | % |
| MD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.31 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.13 | % | |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 7.0 | g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 7.00 | cm3/10min |
| Density / Specific Gravity | ASTMD792 | 1.26 | g/cm³ | |
| ISO1183 | 1.25 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | Break | ASTMD638 | 12 | % |
| Yield | ASTMD638 | 3.0 | % | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 3530 | Mpa |
| Flexural Strength | Break,50.0mmSpan | ASTMD790 | 108 | Mpa |
| Tensile Strength | Yield | ASTMD638 | 63.0 | Mpa |
| Flexural Strength | ISO178 | 95.0 | Mpa | |
| Tensile Modulus | ASTMD638 | 3930 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 48.0 | Mpa |
| Flexural Modulus | ISO178 | 3400 | Mpa | |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 11.0 | mg |
| Tensile Stress | Break | ISO527-2/5 | 45.0 | Mpa |
| Yield | ISO527-2/5 | 60.0 | Mpa | |
| Tensile Strain | Yield | ISO527-2/5 | 5.0 | % |
| Break | ISO527-2/5 | 7.0 | % | |
| Tensile Modulus | ISO527-2/1 | 3300 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 143 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 138 | °C | |
| RTIElec | UL746 | 130 | °C | |
| Evolution Calendar intelligent importer | UL746 | 130 | °C | |
| RTIStr | UL746 | 130 | °C | |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 4.7E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 4E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 8.5E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| Thermal Conductivity | ISO8302 | 0.21 | W/m/K | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass | |
| Heat Deflection Temperature | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 144 | °C |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 136 | °C | |
| Heat Deflection Temperature | 1.8MPa,Annealed | ISO75-2/Ae | 136 | °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 141 | °C |
| -- | ISO306/B120 | 143 | °C | |
| ASTMD152514 | 149 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative Permittivity | 50Hz | IEC60250 | 2.90 | |
| 60Hz | IEC60250 | 2.90 | ||
| 1MHz | IEC60250 | 2.80 | ||
| Comparative Tracking Index | IEC60112 | 150 | V | |
| Dielectric Strength | 0.800mm,in Oil | IEC60243-1 | 33 | KV/mm |
| 1.60mm,in Oil | IEC60243-1 | 25 | KV/mm | |
| 3.20mm,in Oil | IEC60243-1 | 16 | KV/mm | |
| Dissipation Factor? | 50Hz | IEC60250 | 1E-03 | |
| 60Hz | IEC60250 | 1E-03 | ||
| 1MHz | IEC60250 | 0.010 | ||
| Surface Resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C8 | ISO179/1eU | NoBreak | |
| -30°C9 | ISO179/1eU | NoBreak | ||
| -30°C8 | ISO179/1eU | NoBreak | ||
| 23°C9 | ISO179/1eU | NoBreak | ||
| Notched Izod impact strength | 23°C11 | ISO180/1U | NoBreak | |
| 23°C10 | ISO180/1U | NoBreak | ||
| -30°C10 | ISO180/1U | NoBreak | ||
| -30°C11 | ISO180/1U | 130 | kJ/m² | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 61.0 | J |
| Charpy Notched Impact Strength | -30°C8 | ISO179/1eA | 9.0 | kJ/m² |
| 23°C9 | ISO179/1eA | 9.0 | kJ/m² | |
| 23°C8 | ISO179/1eA | 10 | kJ/m² | |
| 23°C | ISO179/2C | 15 | kJ/m² | |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 80 | J/m |
| 23°C | ASTMD256 | 110 | J/m | |
| -30°C10 | ISO180/1A | 8.0 | kJ/m² | |
| -30°C11 | ISO180/1A | 8.0 | kJ/m² | |
| 23°C11 | ISO180/1A | 10 | kJ/m² | |
| 23°C10 | ISO180/1A | 8.0 | kJ/m² | |
| 23°C | ASTMD4812 | 1600 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 115 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | ||
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 | °C |
| Oxygen Index | ISO4589-2 | 37 | % | |
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 825 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.