PC LEXAN™ EXL1433T SABIC INNOVATIVE NANSHA

Unit Price:
$5360 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50.3MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Middle flow High ductility at low tem Short molding cycle
Application Areas:Electronic and Electrical Electronic display Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD：3.20mm	内部方法	0.40to0.80	%
	Modeling Shrinkage	TD：3.20mm	内部方法	0.40to0.80	%
		Modeling Shrinkage	MD:3.20mm	内部方法	0.40到0.80	%
		Modeling Shrinkage	Modeling Shrinkage	TD:3.20mm	内部方法	0.40到0.80	%
Moisture Absorption	Saturation,23°C	ISO62	0.12	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.093	%
Melt Mass-Flow Rate	300°C/1.2kg	ASTMD1238	10	g/10min
Melt Volume flow Rate	300°C/1.2kg	ISO1133	9.50	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus		ISO527-2/1	2350	Mpa
Tensile Modulus		ASTMD638	2220	Mpa
Tensile Strength	Break	ASTMD638	64.1	Mpa
Tensile Strength	Tensile Strength	Yield	ASTMD638	58.0	Mpa
Flexural Modulus	50.0mmSpan	ASTMD790	2220	Mpa
Flexural Strength	Yield,50.0mmSpan	ASTMD790	94.3	Mpa
Tensile Stress	Yield	ISO527-2/50	57.9	Mpa
Tensile Stress	Tensile Stress	Break	ISO527-2/50	61.5	Mpa
Tensile Strain	Yield	ISO527-2/50	5.5	%
Tensile Strain	Tensile Strain	Break	ISO527-2/50	120	%
yield		ISO527-2/50	57.9	Mpa
yield	yield		ISO527-2/50	5.5	%
fracture		ISO527-2/50	120	%
fracture	fracture		ISO527-2/50	61.5	Mpa
Tensile Elongation	Break	ASTMD638	130	%
Yield		ASTMD638	58.0	Mpa
Break		ASTMD638	64.1	Mpa
Flexural Modulus		ISO178	2150	Mpa
50.0mm Span		ASTMD790	2220	Mpa
--7		ISO178	2150	Mpa
--8		ISO178	90.2	Mpa
--1		ASTMD638	2220	Mpa
Yield		ASTMD638	5.8	%
Break		ASTMD638	130	%
Yield,50.0mm Span		ASTMD790	94.3	Mpa
Tensile Elongation	Yield	ASTMD638	5.8	%
Flexural Strength		ISO178	90.2	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Flow:-40 to 95°C		ASTME831	7.2E-05	cm/cm/°C
Flow:-40 to 95°C		ASTME831	7.9E-05	cm/cm/°C
1.8MPa, Unannealed,64.0mm Span		ISO75-2/Af	119	°C
RTI		UL746	130	°C
Heat Deflection Temperature	1.8MPa,Unannealed,64.0mmSpan	ISO75-2/Af	119	°C
--		ASTMD1525,ISO306/B501116	141	°C
--	--		ISO306/B120	142	°C
Flow:23 to 80°C		ISO11359-2	7.2E-05	cm/cm/°C
Flow:23 to 80°C		ISO11359-2	7.9E-05	cm/cm/°C
1.8MPa, Unannealed,3.20mm		ASTMD648	124	°C
Ball PressureTest	125°C	IEC60695-10-2	Pass
RTIElec		UL746	130	°C
RTIStr		UL746	130	°C
Linear thermal expansion coefficient	MD：23to80°C	ISO11359-2	7.2E-05	cm/cm/°C
	Linear thermal expansion coefficient	TD：-40to95°C	ASTME831	7.9E-05	cm/cm/°C
		Linear thermal expansion coefficient	TD：23to80°C	ISO11359-2	7.9E-05	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	MD：-40to95°C	ASTME831	7.2E-05	cm/cm/°C
Deflection Temperature Under Load?	1.8MPa,Unannealed,3.20mm	ASTMD648	124	°C
Vicat Softening Temperature		ASTMD152510	141	°C
	Vicat Softening Temperature	--	ISO306/B50	141	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B120	142	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		ASTMD257	>1.0E+15	ohms
Volume Resistivity		ASTMD257	>1.0E+15	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	-30°C,TotalEnergy	ASTMD3763	85.0	J
Instrumented Dart Impact	Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	82.4	J
Charpy Notched Impact Strength	-30°C	ISO179/1eA	50	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	70	kJ/m²
-30°C12		ISO180/1A	45	kJ/m²
23°C13		ISO180/1A	65	kJ/m²
-30°C		ASTMD256	800	J/m
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	无断裂
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	无断裂
Unnotched Izod Impact Strength	-30°C	ISO180/1U	无断裂
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C	ISO180/1U	无断裂
23°C		ASTMD256	890	J/m
Unnotched Izod Impact Strength	-30°C	ISO180/1U	NoBreak
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C	ISO180/1U	NoBreak
Charpy Notched Impact Strength	-30°C	ISO179/1eA	50	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	70	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	NoBreak
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	NoBreak
Notched Izod Impact Strength	-30°C	ISO180/1A	45	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	65	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	L-Sale	ASTMD785	90
Rockwell Hardness	Rockwell Hardness	L-Sale	ISO2039-2	90

optical performance	Test Condition	Test Method	Test Result	Unit
Transmittance	2540µm	ASTMD1003	82.0	%
Haze	2540µm	ASTMD1003	3.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	2.5mm	UL94	V-2
	UL flame retardant rating	3.0mm,TestingbySABIC	UL94	V-2
	UL flame retardant rating	UL flame retardant rating	2.50mm	UL94	V-2
Glow Wire Flammability Index	3.0mm	IEC60695-2-12	960	°C
Glow Wire Flammability Index	Glow Wire Flammability Index	3.00mm	IEC60695-2-12	960	°C
Glow Wire Ignition Temperature	0.800mm	IEC60695-2-13	825	°C
	Glow Wire Ignition Temperature	3.00mm	IEC60695-2-13	825	°C
		Glow Wire Ignition Temperature	0.8mm	IEC60695-2-13	825	°C
		Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0mm	IEC60695-2-13	825	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.