Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | ASTM D955 | % | 0.4－0.6 |
| Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | g/10min | 300℃/1.2kg,7.5 |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | % | 0.31 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ASTM D638/ISO 527 | kg/cm²(MPa)[Lb/in²] | 479000 |
| Tensile Strength | | ASTM D638/ISO 527 | kg/cm²(MPa)[Lb/in²] | 8270/6960 |
| Tensile Elongation | | ASTM D638/ISO 527 | % | |
| Flexural Modulus | | ASTM D790/ISO 178 | kg/cm²(MPa)[Lb/in²] | 453000（493000） |
| Flexural Strength | | ASTM D790/ISO 178 | kg/cm²(MPa)[Lb/in²] | 1360（13800） |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying conditions | | | | 干燥温度：248℉，干燥时间：2.0to4.0 hr |
| Melt Temperature | | | ℃ | 554-608 |
| Mold Temperature | | | ℃ | 176-248 |
| Processing temperature | | | ℃ | 518-572 |
| Processing temperature | | | ℃ | 554-608 |
| Processing temperature | | | ℃ | 536-590 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy impact strength | | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | 44565 |
| Izod notch impact strength | | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | 缺口：2.5 |
| Izod notch impact strength | | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | 缺口：1.9 |
| Izod notch impact strength | | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | 44570 |
| Tensile Elongation?(Break) | | ASTM D638/ISO 527 | % | |
| Electrical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | ASTM D257/IEC 60093 | Ω.cm | >1.0E+15 ohm.cm |
| Surface Resistivity | | ASTM D257/IEC 60093 | Ω | >1.0E+15 ohms |
| Dielectric Constant | | ASTM D150/IEC 60250 | | 50HZ/60HZ:2.9 |
| Dielectric Constant | | ASTM D150/IEC 60250 | | 2.8 |
| Dielectric loss | | ASTM D150/IEC 60250 | | 0.001 |
| Dielectric loss | | ASTM D150/IEC 60250 | | 0.01 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning Rate | | UL94 | | V1-V0 |
| Vicat Softening Temperature | | ASTM D1525/ISO R306 | ℃（℉） | 309 |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | mm/mm.℃ | 0.000026－0.000047 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.