Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.50to0.70 | % |
Moisture Absorption | 24hr | ASTMD570 | 0.10 | % |
Moisture Absorption | Equilibrium,23°C | ASTMD570 | 0.35 | % |
Moisture Absorption | Equilibrium,100°C | ASTMD570 | 0.58 | % |
Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 25 | g/10min |
Density / Specific Gravity | | ASTMD792 | 1.20 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | Yield | ASTMD638 | 62.1 | Mpa |
Tensile Strength | Break | ASTMD638 | 65.5 | Mpa |
Tensile Elongation | Break | ASTMD638 | 120 | % |
Flexural Modulus | 50.0mmSpan | ASTMD790 | 2310 | Mpa |
Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 93.1 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
RTIElec | | UL746 | 130 | °C |
Evolution Calendar intelligent importer | | UL746 | 130 | °C |
RTIStr | | UL746 | 130 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 127 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Comparative Tracking Index | CTI | UL746 | PLC2 | |
Hot-wire Ignition | HWI | UL746 | PLC2 | |
High Amp Arc Ignition | HAI | UL746 | PLC1 | |
High Voltage Arc Tracking Rate | HVTR | UL746 | PLC2 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Impact Strength | | ASTMD1822 | 378 | kJ/m² |
Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 54.2 | J |
Notched Izod Impact Strength | 23°C | ASTMD256 | 640 | J/m |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Haze | 2540µm | ASTMD1003 | 1.0 | % |
Transmittance | 2540µm | ASTMD1003 | 88.0 | % |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.1mm | UL94 | V-2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.