PC PANLITE® L-1225Z100 TEIJIN JAPAN

Unit Price:
$2081 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:UV resistance transparent
Application Areas:Translucent accessories lens Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Method	Test Result	Unit
Density	ASTM D792/ISO 1183	/1200
Modeling Shrinkage	ASTM D955	0.5-0.7	%
Moisture Absorption 23℃/24H	ASTM D570/ISO 62	0.2	%

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD:4.00mm	内部方法	0.50to0.70	%
Modeling Shrinkage	Modeling Shrinkage	MD:4.00mm	内部方法	0.50to0.70	%
Moisture Absorption	23°C,24hr	ISO62	0.20	%
Melt Volume flow Rate	300°C/1.2kg	ISO1133	12.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Yield	ISO527-2/50	61.0	Mpa
Tensile Strain	Yield	ISO527-2/50	6.0	%
Flexural Modulus		ISO178	2400	Mpa
Flexural Stress		ISO178	94.0	Mpa
Nominal Tensile Strain at Break		ISO527-2/50	>50	%
Tensile Modulus		ASTM D638/ISO 527	/2400	kg/cm²(MPa)[Lb/in²]
Tensile Modulus	Tensile Modulus		ISO527-2/1	2400	Mpa
Tensile Strength		ASTM D638/ISO 527	/61	kg/cm²(MPa)[Lb/in²]
Tensile Elongation		ASTM D638/ISO 527	/6	%
Flexural Modulus		ASTM D790/ISO 178	/2400	kg/cm²(MPa)[Lb/in²]
Flexural Strength		ASTM D790/ISO 178	/94	kg/cm²(MPa)[Lb/in²]

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	141	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	128	°C
Vicat Softening Temperature		ASTM D1525/ISO R306	148	℃（℉）
Linear expansion coefficient		ASTM D696/ISO 11359	0.7	mm/mm.℃
Vicat Softening Temperature		ISO306/B50	148	°C
Linear thermal expansion coefficient	MD	ISO11359-2	7E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	7E-05	cm/cm/°C
RTIElec	1.5mm	UL746	125	°C
Evolution Calendar intelligent importer	1.5mm	UL746	115	°C
RTIStr	1.5mm	UL746	125	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation Factor?	100Hz	IEC60250	1E-03
Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	9E-03
Relative Permittivity	100Hz	IEC60250	3.10
Relative Permittivity	Relative Permittivity	1MHz	IEC60250	3.00
Comparative Tracking Index		IEC60112	250	V
Surface Resistivity		IEC60093	>1.0E+15	ohms
Dielectric Constant		ASTM D150/IEC 60250	3.1
Dielectric Constant	Dielectric Constant		ASTM D150/IEC 60250	3
Volume Resistivity		IEC60093	>1.0E+15	ohms·cm
Dielectric Strength		IEC60243-1	30	KV/mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength		ISO179	NoBreak

optical performance	Test Condition	Test Method	Test Result	Unit
Transmittance	3000µm	ASTMD1003	88.0	%
Transmittance		ASTM D1003/ISO 13468	88	%
Refractive index of light		ASTM D542/ISO 489	1.585
Refractive index of light	Refractive index of light		ASTMD542	1.585

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.40mm	UL94	V-2
UL flame retardant rating	UL flame retardant rating	1.9mm	UL94	HB
Glow Wire Flammability Index	1.5mm	IEC60695-2-12	825	°C
Glow Wire Flammability Index	Glow Wire Flammability Index	3.2mm	IEC60695-2-12	875	°C
Glow Wire Ignition Temperature	1.5mm	IEC60695-2-13	850	°C
Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.2mm	IEC60695-2-13	875	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.