Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.42 | |
| Modeling Shrinkage | | ASTM D955 | 1.5 | % |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.11 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Spiral Flow | 3mm厚 | 出光法 | 23 | CM |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation | | ISO R-527 (ASTM D-638) | 8100(83000) | MPa(KG/cm |
| Tensile Elongation?(Break) | | ISO R-527 (ASTM D-638) | 3 | % |
| Tensile Strength (Break) | | ISO R-527 (ASTM D-638) | 120(1200) | MPa(KG/cm |
| Flexural strength | | ISO 178 (ASTM D-790) | 170(1700) | Mpa |
| Tensile Modulus | | ISO 178 (ASTM D-790) | 8530(8700) | MPa(KG/cm |
| Tensile Strength | | ASTM D638/ISO 527 | 8100(83000) | kg/cm²(MPa)[Lb/in²] |
| Rockwell Hardness | | ASTM D785 | M92 | |
| Rockwell Hardness | | ISO 2039-2 (ASTM D-785) | M92 | |
| Flexural Modulus | | ASTM D790/ISO 178 | 8530(8700) | kg/cm²(MPa)[Lb/in²] |
| Flexural Strength | | ASTM D790/ISO 178 | 170(1700) | kg/cm²(MPa)[Lb/in²] |
| Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 3 | % |
| Izod Impact Strength | 4mm with notch 3.2mm with notch | ISO 180 (ASTM D-256) | 15(16) | KJ/m |
| Izod notch impact strength | | ASTM D256/ISO 179 | 15(16) | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Coefficient of Linear Thermal Expansion | | ASTM D-696 | 2.3 | |
| Heat Deflection Temperature | 1.80MPa,18.6kg/cm | ISO 75(ASTM D-648) | 144 | °C |
| Flammability | 1.47mm厚 | UL 94 | V-2 | |
| Burning Rate | | UL94 | V-2 | |
| Vicat Softening Temperature | | ASTM D1525/ISO R306 | 150 | ℃（℉） |
| Vicat Softening Temperature | | ISO 306 | 150 | °C |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 2.3 | mm/mm.℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Arc Resistance | | ASTM D-495 | 110 | sec |
| Dielectric Constant | 60Hz | ASTM D-150 | 8×10 | |
| Dielectric Constant | 10 | ASTM D-150 | 9×10 | |
| Volume Resistivity | | ASTM D-257 | ＜10 | Ω·cm |
| Insulation Resistance | 1.6mm厚 | ASTM D-149 | ＜22 | KV/mm |
| Dissipation Factor | 10 | ASTM D-150 | 3.45 | |
| Dissipation Factor | 60Hz | ASTM D-150 | 3.40 | |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD | ASTM D-955 | 1.5 | |
| Modeling Shrinkage | TD | ASTM D-955 | 6.0 | |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 23℃水中24h | ASTM D-570 | 0.11 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.