Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant transparent
Application Areas:Non specific food Nursing supplies Medical supplies
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24 hr	ASTM D570	0.15	%
	Moisture Absorption	Equilibrium, 23°C	ASTM D570	0.35	%
	Moisture Absorption	Moisture Absorption	Equilibrium, 100°C	ASTM D570	0.58	%
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	11	g/10 min
Melt Volume flow Rate	300°C/1.2 kg	ISO 1133	10.0	cm3/10min
Specific Volume		ASTM D792	0.830	cm³/g
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Stress	-- 5, 6	ISO 178	90.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	97.0	Mpa
Taber Abrasion Resistance	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg
Tensile Strength	Yield 3	ASTM D638	62.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	63.0	Mpa
		Tensile Strength	Break 3	ASTM D638	68.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	70.0	Mpa
Tensile Modulus	-- 2	ASTM D638	2370	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2350	Mpa
Tensile Elongation	Yield 3	ASTM D638	7.0	%
	Tensile Elongation	Yield	ISO 527-2/50	6.0	%
		Tensile Elongation	Break 3	ASTM D638	130	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	110	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2340	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2300	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D152511	154	°C
	Vicat Softening Temperature	--	ISO 306/A50	153	°C
		Vicat Softening Temperature	--	ISO 306/B50	141	°C
		Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	142	°C
Specific Heat		ASTM C351	1250	J/kg/°C
Thermal Conductivity	--	ASTM C177	0.19	W/m/K
Thermal Conductivity	Thermal Conductivity	--	ISO 8302	0.20	W/m/K
RTI		UL 746	130	°C
RTI Imp		UL 746	130	°C
RTI Elec		UL 746	130	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 10	ISO 75-2/Be	136	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	132	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 10	ISO 75-2/Ae	125	°C
Ball PressureTest	123 to 127°C	IEC 60695-10-2	通过
Coefficient of Linear Thermal Expansion (Flow)	-40 to 95°C	ASTM E831	6.8E-5	cm/cm/°C
Coefficient of Linear Thermal Expansion (Flow)	Coefficient of Linear Thermal Expansion (Flow)	23 to 80°C	ISO 11359-2	7.0E-5	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		UL 746	PLC 2
Hot-wire Ignition		UL 746	PLC 2
High Voltage Arc Tracking Rate		UL 746	PLC 2
High Amp Arc Ignition		UL 746	PLC 1
Dielectric Strength	3.20 mm, in Air	ASTM D149	15	KV/mm
Dielectric Strength	Dielectric Strength	3.20 mm, in Oil	IEC 60243-1	17	KV/mm
Dissipation Factor?	50 Hz	ASTM D150	9.0E-4
	Dissipation Factor?	60 Hz	ASTM D150	9.0E-4
		Dissipation Factor?	1 MHz	ASTM D150, IEC 60250	0.010
			Dissipation Factor?	50 Hz	IEC 60250	1.0E-3
			Dissipation Factor?	Dissipation Factor?	60 Hz	IEC 60250	1.0E-3
Surface Resistivity		IEC 60093	> 1.0E+15	ohms
Dielectric Constant	60 Hz	ASTM D150	3.17
	Dielectric Constant	50 kHz	ASTM D150	3.17
		Dielectric Constant	1 MHz	ASTM D150	2.96
			Dielectric Constant	50 Hz	IEC 60250	2.70
				Dielectric Constant	60 Hz	IEC 60250	2.70
				Dielectric Constant	Dielectric Constant	1 MHz	IEC 60250	2.70
Volume Resistivity	--	ASTM D257	> 1.0E+17	ohms·cm
Volume Resistivity	Volume Resistivity	--	IEC 60093	> 1.0E+15	ohms·cm

Injection	Test Result	Unit
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	270 到 295	°C
Middle Temperature	280 到 305	°C
Front Temperature	295 到 315	°C
Nozzle Temperature	290 到 310	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	295 到 315	°C
Mold Temperature	70 到 95	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Gardner Impact	23°C	ASTM D3029	169	J
Instrumented Dart Impact	23°C, Energy at Peak	ASTM D3763	63.0	J
Tensile Impact Strength		ASTM D1822	577	kJ/m²
Unnotched Izod Impact Strength	23°C	ASTM D4812	3200	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTM D785	70
Rockwell Hardness	Rockwell Hardness	R-Scale	ASTM D785	118

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index of light		ASTM D542	1.586
Transmittance	2540 µm	ASTM D1003	88.0	%
Haze	2540 µm	ASTM D1003	1.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
Oxygen Index		ASTM D2863, ISO 4589-2	25	%
Flame Rating	1.5 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.