Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ISO294-4 | 0.50to0.70 | % |
Density/Specific Gravity 2 | | ASTMD792 | 1.20 | g/cm³ |
Density / Specific Gravity | 23°C | ISO1183 | 1.20 | g/cm³ |
Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 62 | g/10min |
Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 65.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | Yield | ASTMD638 | 61.6 | Mpa |
Flexural Modulus | | ASTMD790 | 2340 | Mpa |
Flexural Strength | | ASTMD790 | 89.8 | Mpa |
Tensile Elongation | Break | ASTMD638 | 70 | % |
Flexural Modulus | | ISO178 | 2400 | Mpa |
Flexural Stress | | ISO178 | 90.0 | Mpa |
Tensile Stress | Yield | ISO527-2/50 | 60.0 | Mpa |
Tensile Stress | Break | ISO527-2/50 | 50.0 | Mpa |
Tensile Strain | Break | ISO527-2/50 | 65 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD | ISO11359-2 | 6.0E-5to8.0E-5 | cm/cm/°C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 124 | °C |
Deflection Temperature Under Load? | 1.8MPa,Annealed | ISO75-2/A | 140 | °C |
Vicat Softening Temperature | | ASTMD15256 | 150 | °C |
Vicat Softening Temperature | -- | ISO306/A50 | 145 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 140 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | 23°C | ISO179 | 10 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/1A | 8.0 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M-Scale | ASTMD785 | 77 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.