PC Makrolon® 6555 COVESTRO GERMANY

185

Unit Price:
$2501 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
46MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Medium viscosity
Application Areas:Electrical field Electronic field Industrial applications
Color:--
Grade:Flame retardant grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD	ISO2577	0.60to0.80	%
	Shrinkage rate	MD	ISO2577	0.60to0.80	%
		Shrinkage rate	TD:2.00mm3	ISO294-4	0.75	%
		Shrinkage rate	Shrinkage rate	MD:2.00mm3	ISO294-4	0.70	%
Water absorption rate	Saturation,23°C	ISO62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.12	%
Melt mass flow rate	300°C/1.2kg	ISO1133	10	g/10min
Melt volume flow rate	300°C/1.2kg	ISO1133	10.0	cm3/10min
Density/specific gravity	23°C	ISO1183	1.20	g/cm³
Apparent density 2		ISO60	0.64	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Nominal tensile fracture strain	23°C	ISO527-2/50	>50	%
TensileCreepModule	1hr	ISO899-1	2200	Mpa
Tensile stress	Yield,23°C	ISO527-2/50	66.0	Mpa
Tensile stress	Tensile stress	Break,23°C	ISO527-2/50	70.0	Mpa
Tensile strain	Yield,23°C	ISO527-2/50	6.2	%
Tensile strain	Tensile strain	Break,23°C	ISO527-2/50	130	%
Tensile creep modulus	1000hr	ISO899-1	1900	Mpa
Tensile modulus	23°C	ISO527-2/1	2400	Mpa
Bending stress 4	3.5%Strain,23°C	ISO178	74.0	Mpa
Bending stress 4	Bending stress 4	23°C	ISO178	98.0	Mpa
Bending modulus 4	23°C	ISO178	2400	Mpa
Bending strain 5	23°C	ISO178	7.1	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Glass transition temperature 8		ISO11357-2	145	°C
Thermal conductivity coefficient 9	23°C	ISO8302	0.20	W/m/K
BallPressure Test	136°C	IEC60695-10-2	Pass
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	137	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	125	°C
RTIElec	1.5mm	UL746	125	°C
Evolution Calendar intelligent importer	1.5mm	UL746	115	°C
RTIStr	1.5mm	UL746	125	°C
Vicat softening temperature	--	ISO306/B50	144	°C
Vicat softening temperature	Vicat softening temperature	--	ISO306/B120	145	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO11359-2	6.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO11359-2	6.5E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength	23°C,1.00mm	IEC60243-1	34	KV/mm
Dissipation factor	23°C,100Hz	IEC60250	8E-04
Dissipation factor	Dissipation factor	23°C,1MHz	IEC60250	9E-03
Relative permittivity	23°C,100Hz	IEC60250	3.10
Relative permittivity	Relative permittivity	23°C,1MHz	IEC60250	3.00
Leakage Trace Index	SolutionA	IEC60112	225	V
Leakage Trace Index	Leakage Trace Index	SolutionB	IEC60112	125	V
Surface resistivity		IEC60093	1E+16	ohms
Volume resistivity	23°C	IEC60093	1E+16	ohms·cm

film	Test Condition	Test Method	Test Result	Unit
WaterVaporTransmission Rate	23°C,85%RH,100µm	ISO15106-1	15	g/m²/24hr
GasPermeation	CarbonDioxide:23°C,25.4µm	ISO2556	16900	cm³/m²/bar/24hr
	GasPermeation	CarbonDioxide:23°C,100.0µm	ISO2556	4300	cm³/m²/bar/24hr
		GasPermeation	Nitrogen:23°C,25.4µm	ISO2556	510	cm³/m²/bar/24hr
			GasPermeation	Nitrogen:23°C,100.0µm	ISO2556	130	cm³/m²/bar/24hr
				GasPermeation	Oxygen:23°C,25.4µm	ISO2556	2760	cm³/m²/bar/24hr
				GasPermeation	GasPermeation	Oxygen:23°C,100.0µm	ISO2556	700	cm³/m²/bar/24hr

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam gap 6	-30°C,Complete Break	ISO7391	14	kJ/m²
Impact strength of simply supported beam gap 6	Impact strength of simply supported beam gap 6	23°C,Partial Break	ISO7391	70	kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO6603-2	65.0	J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO6603-2	60.0	J
Suspended wall beam gap impact strength 7	-30°C,Complete Break	ISO7391	12	kJ/m²
Suspended wall beam gap impact strength 7	Suspended wall beam gap impact strength 7	23°C,Partial Break	ISO7391	65	kJ/m²
Multi axis Instrumented Peak Impact Force	-30°C	ISO6603-2	6300	N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23°C	ISO6603-2	5400	N
Impact strength of simply supported beam without notch	-60°C	ISO179/1eU	NoBreak
	Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	NoBreak
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO2039-1	115	Mpa

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive Index11		ISO489	1.586
transmissivity	1000µm	ISO13468-2	89.0	%
	transmissivity	2000µm	ISO13468-2	89.0	%
		transmissivity	3000µm	ISO13468-2	88.0	%
		transmissivity	transmissivity	4000µm	ISO13468-2	87.0	%

flammability	Test Condition	Test Method	Test Result	Unit
ApplicationofFlamefromSmallBurner MethodKandF	2.00mm	DIN53438-1,-3	K1,F1
Burning rate - US-FMVSS	>1.00mm	ISO3795	passed
FlashIgnitionTemperature		ASTMD1929	460	°C
GlowWireTest	1.50mm	EDFHN60E.02	750	°C
GlowWireTest	GlowWireTest	3.00mm	EDFHN60E.02	750	°C
Needle flame test	MethodF:1.50mm	IEC60695-11-5	2.0	min
	Needle flame test	MethodF:2.00mm	IEC60695-11-5	2.0	min
		Needle flame test	MethodF:3.00mm	IEC60695-11-5	2.0	min
			Needle flame test	MethodK:1.50mm	IEC60695-11-5	1.0	min
				Needle flame test	MethodK:2.00mm	IEC60695-11-5	2.0	min
				Needle flame test	Needle flame test	MethodK:3.00mm	IEC60695-11-5	2.0	min
Extreme Oxygen Index 10		ISO4589-2	35	%
SelfIgnition		ASTMD1929	530	°C
Hot filament ignition temperature	0.75mm	IEC60695-2-13	875	°C
	Hot filament ignition temperature	1.5mm	IEC60695-2-13	875	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC60695-2-13	875	°C
UL flame retardant rating	1.0mm	UL94	V-2
UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	V-0
Burning wire flammability index	0.75mm	IEC60695-2-12	875	°C
	Burning wire flammability index	1.5mm	IEC60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC60695-2-12	960	°C

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ElectrolyticalCorrosion	23°C	IEC60426	A1
ISO Shortcut			ISO7391-PC,MFR,(,,)-09-9

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.